PA66 Akulon® K224-G6 DSM HOLAND
217
- Unit Price:US$ 3,254 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:65.5MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Glass fiber reinforced｜Filler: Glass fiber reinforced material｜30%｜Filler by weight
- Application Areas:Insulation material｜Shell｜furniture｜wheel
- Color:--
- Grade:Enhanced level
Material Certification
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO 75-2/B | 220 °C |
| 1.8MPa,未退火 | ISO 75-2/A | 200 °C | |
| melting temperature | ISO 11357-3 | 220 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 2E-05 cm/cm/°C |
| TD | ISO 11359-2 | 7E-05 cm/cm/°C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Hot filament ignition temperature | 2.0mm | IEC 60695-2-13 | 725 °C |
| UL flame retardant rating | 0.75mm | IEC 60695-11-10,-20 | HB |
| 1.5mm | IEC 60695-11-10,-20 | HB | |
| Burning wire flammability index | 1.5mm | IEC 60695-2-12 | 700 °C |
| 2.0mm | IEC 60695-2-12 | 700 °C | |
| Hot filament ignition temperature | 1.5mm | IEC 60695-2-13 | 725 °C |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 75 kJ/m² |
| 23°C | ISO 179/1eU | 90 kJ/m² |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| shrinkage rate | MD | ISO 294-4 | 0.30 % |
| Water absorption rate | 饱和,23°C | ISO 62 | 6.3 % |
| 平衡,23°C,50%RH | ISO 62 | 1.9 % | |
| shrinkage rate | TD | ISO 294-4 | 0.90 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| relative permittivity | 100Hz | IEC 60250 | 3.50 |
| 1MHz | IEC 60250 | 3.30 | |
| Dissipation Factor | 100Hz | IEC 60250 | 5E-03 |
| 1MHz | IEC 60250 | 0.015 | |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | V | |
| Surface Resistivity | IEC 60093 | -- ohms | |
| volume resistivity | IEC 60093 | 1E+15 ohms·cm | |
| dielectric strength | IEC 60243-1 | 30 KV/mm |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 9500 Mpa | |
| tensile strength | 断裂 | ISO 527-2 | 180 Mpa |
| Tensile strain | 断裂 | ISO 527-2 | 3.5 % |
| flexural modulus | ISO 178 | 8600 Mpa | |
| bending strength | ISO 178 | 235 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.