Material Description

Material Properties:--
Application Areas:--
Color:--
Grade:Flame retardant enhanced grade

Technical Data Sheet

flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	3.0 mm	UL 94	V-0
	UL flame retardant rating	1.5 mm	UL 94	V-0
	UL flame retardant rating	UL flame retardant rating	0.8 mm	UL 94	V-0
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength	23°C, 3.20 mm, Injection	ASTM D790	196	Mpa
Bending modulus	23°C, 3.20 mm, Injection	ASTM D790	8340	Mpa
elongation	Break, 23°C, 3.20 mm, Injection	ASTM D638	3.0	%
tensile strength	Break, 23°C, 3.20 mm, Injection	ASTM D638	123	Mpa
injection	Test Condition	Test Method	Test Result	Test Unit
drying temperature			80 to 100	°C
drying time			4.0 to 5.0	hr
Suggested maximum moisture content			0.10	%
Temperature at the rear of the barrel			265 to 275	°C
Mold temperature			80 to 110	°C
Temperature in the middle of the barrel			270 to 280	°C
Temperature at the front of the material cylinder			270 to 285	°C
Spray nozzle temperature			270 to 280	°C
Processing (melt) temperature			270 to 290	°C
Back pressure			0.981 to 2.94	Mpa
Screw speed			60 to 150	rpm
thermal performance	Test Condition	Test Method	Test Result	Test Unit
RTI	3.0 mm	UL 746	65.0	°C
	RTI	1.5 mm	UL 746	65.0	°C
	RTI	RTI	0.8 mm	UL 746	65.0	°C
RTI Imp	3.0 mm	UL 746	65.0	°C
	RTI Imp	1.5 mm	UL 746	65.0	°C
	RTI Imp	RTI Imp	0.8 mm	UL 746	65.0	°C
RTI Elec	3.0 mm	UL 746	65.0	°C
	RTI Elec	1.5 mm	UL 746	65.0	°C
	RTI Elec	RTI Elec	0.8 mm	UL 746	65.0	°C
Linear coefficient of thermal expansion	Flow	ASTM D696	3.0E-5	cm/cm/°C
Melting temperature		ASTM D3418	260	°C
Hot deformation temperature	1.8 MPa, Unannealed, 6.40 mm, Injection	ASTM D648	225	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	24 hr, 23°C	ASTM D570	0.70	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dielectric constant	23°C, 1 MHz	ASTM D150	3.00
Dielectric strength	23°C, 1.00 mm	ASTM D149	22	KV/mm
Volume resistivity	23°C	ASTM D257	1.0E+14	ohms·cm
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Scale, 23°C, Injection	ASTM D785	125

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

PA66 LUMID® GN-2251BF LG CHEM KOREA

Material Description

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index