POM

POM TENAC™ LT804 ASAHI JAPAN

233

Unit Price:US$ 3,584 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
59MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High sliding｜wear resistant
Application Areas:Keyboard and mouse｜Office supplies｜Engine parts
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet

other	Test Condition	Test Method	Test Result
characteristic			对金属有优异的耐摩擦和耐耗

mechanical properties	Test Condition	Test Method	Test Result
Bending modulus		ASTM D790/ISO 178	2740 kg/cm²(MPa)[Lb/in²]
Rockwell hardness		ASTM D785	92
elongation		ASTM D638/ISO 527	60 %
tensile strength		ASTM D638/ISO 527	64 kg/cm²(MPa)[Lb/in²]
Wear resistance		ASTM D1044	13
Rockwell hardness	-	ASTM D785	120 R
Rockwell hardness	Rockwell hardness	-	ASTM D785	92 M
Impact strength of cantilever beam gap		ASTM D256	78 J/m
Bending modulus		ASTM D790	2740 Mpa
bending strength		ASTM D790	91 Mpa
Elongation at Break		ASTM D638	60 %
tensile strength		ASTM D638	64 Mpa
bending strength		ASTM D790/ISO 178	91 kg/cm²(MPa)[Lb/in²]

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion		ASTM D696/ISO 11359	10 mm/mm.℃
Hot deformation temperature	HDT	ASTM D648/ISO 75	125 ℃（℉）
Linear coefficient of thermal expansion		TMA法	10
melt mass-flow rate		ASTM D1238	9 g/10min
Combustibility (rate)		UL 94	HB
UL flame retardant rating		UL 94	HB
Hot deformation temperature	0.45MPa	ASTM D648	172 °C
Hot deformation temperature	Hot deformation temperature	1.82MPa	ASTM D648	125 °C

Physical properties	Test Condition	Test Method	Test Result
density		ASTM D792/ISO 1183	1.42
melt mass-flow rate		ASTM D1238/ISO 1133	9 g/10min
Shrinkage rate	Flow	旭化成法	1.8-2.2 %
Water absorption rate		ASTM D570	0.2 %
Shrinkage rate	Across Flow	旭化成法	1.8-2.2 %
melt mass-flow rate		ASTM D1238/ISO 1133	0.2 g/10min

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.