ABS KINGFA® KF-730 KINGFA LIAONING
1035
- Unit Price:US$ 1,384 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:788.6MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Universal level｜Wide application range
- Application Areas:Office equipment application｜Electronic and Electrical Applications｜Home appliance applications
- Color:--
- Grade:General grade
Material Certification
TDS
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 23℃ | ISO 1183-1 | 1.05 g/cm³ | |
| melt mass-flow rate | ISO 1133-1 | 2 g/10min | |
| 220℃, 10kg | ISO 1133-1 | 20 g/10min | |
| 23℃ | ISO 2577 | 0.4-0.7 % | |
| melt mass-flow rate | ISO 1133-1 | 2 g/10min | |
| ISO 1133-1 | 20 g/10min | ||
| Shrinkage rate | ISO 2577 | 0.4-0.7 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 50mm/min?? | ISO 527-2 | 47 Mpa | |
| 50mm/min? | ISO 527-2 | 8 % | |
| 2mm/min?? | ISO 178 | 76 Mpa | |
| ISO 178 | 2500 Mpa | ||
| Rockwell hardness | ISO 2039-2 | 108 R scale | |
| tensile strength | ISO 527-2 | 47 Mpa | |
| fracture | ISO 527-2 | 8 % | |
| bending strength | ISO 178 | 76 Mpa | |
| Flexural modulus | ISO 178 | 2500 Mpa | |
| Rockwell hardness | ISO 2039-2 | 108 R scale |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 23℃ | ISO 180 | 20 kJ/m² | |
| Impact strength of cantilever beam gap | ISO 180 | 20 kJ/m² |
| Flame retardant performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 1.6mm | UL 94 | HB | |
| UL flame retardant rating | UL 94 | HB |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Volume resistivity | IEC 60093 | 100000000000000 ohms·cm | |
| dielectric strength | IEC 60243-1 | 22 KV/mm | |
| Volume resistivity | IEC 60093 | 100000000000000 ohms·cm | |
| dielectric strength | IEC 60243-1 | 22 KV/mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 0.45MPa?? | ISO 75-2 | 85 °C | |
| 1.8MPa?? | ISO 75-2 | 77 °C | |
| 1kg, 120℃/h?? | ISO 306 | 96 °C | |
| 5kg, 50℃/h | ISO 306 | 86 °C | |
| Hot deformation temperature (HDT) | ISO 75-2 | 85 °C | |
| ISO 75-2 | 77 °C | ||
| vicat | ISO 306 | 96 °C | |
| ISO 306 | 86 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.