PC DX10311-701 SABIC INNOVATIVE NANSHA
177
- Unit Price:US$ 7,757 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Filler: Glass fiber reinforced material｜30% filler by weight
- Application Areas:--
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,未退火,3.20mm | ASTM D648 | 128 °C |
| Linear coefficient of thermal expansion | MD:-40到40°C | ASTME831 | 1.9E-05 cm/cm/°C |
| TD:-40到40°C | ASTME831 | 6.4E-05 cm/cm/°C |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/2U | 57 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ASTM D4812 | 750 J/m |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Melt volume flow rate | 300°C/5.0kg | ISO 1133 | 37.0 cm3/10min |
| shrinkage rate | MD:3.20mm | 内部方法 | 0.10-0.30 % |
| TD:3.20mm | 内部方法 | 0.20-0.40 % |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| --1 | ASTM D638 | 8340 Mpa | |
| fracture | ASTM D638 | 117 Mpa | |
| ISO 527-2/5 | 119 Mpa | ||
| ASTM D638 | 2.6 % | ||
| ISO 527-2/5 | 2.7 % | ||
| --4 | ISO 178 | 7730 Mpa | |
| --5 | ISO 178 | 182 Mpa | |
| --6 | ISO 178 | 181 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.