PA66 AKROMID® A3GF15 AKRO-PLASTIC GERMANY
269
- Unit Price:US$ 3,273 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:20MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Glass fiber reinforced
- Application Areas:Automotive sector｜Electronic field｜Electrical field
- Color:--
- Grade:--
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ball-indentation hardness | H961/30 | ISO 2039-1 | 200 Mpa |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO 75-2/B | 260 °C |
| 1.8MPa,未退火 | ISO 75-2/A | 245 °C | |
| melting temperature | DIN EN11357-1 | 262 °C | |
| Linear coefficient of thermal expansion | MD：23到80°C | ISO 11359-2 | 3.4E-05 cm/cm/°C |
| TD：23to80°C | ISO 11359-2 | 1.1E-04 cm/cm/°C | |
| TemperatureIndex | 50%LossofTensileStrength,20000hr | IEC 216 | 130to150 °C |
| 50%LossofTensileStrength,5000hr | IEC 216 | 160to175 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| burning rate | 1.00mm | FMVSS302 | <100 mm/min |
| UL flame retardant rating | 0.8mm | UL 94 | HB |
| Burning wire flammability index | 1.6mm | IEC 60695-2-12 | 650 °C |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ReinforcementContent | ISO 1172 | 15 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 43 kJ/m² |
| 23°C | ISO 179/1eU | 45 kJ/m² |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| spiral flow length | 内部方法 | 99.0 CM | |
| shrinkage rate | TD | ISO 294-4 | 1.4 % |
| MD | ISO 294-4 | 0.40 % | |
| Water absorption rate | 饱和,23°C | ISO 62 | 6.7to7.3 % |
| moisture absorption | 70°C，62%RH | ISO 1110 | 2.5to2.7 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | 1E+12 ohms | |
| volume resistivity | IEC 60093 | 1E+13 ohms·cm | |
| Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | V |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 6400 Mpa | |
| tensile strength | 断裂 | ISO 527-2/5 | 140 Mpa |
| Tensile strain | 断裂 | ISO 527-2/5 | 3.5 % |
| flexural modulus | ISO 178 | 6100 Mpa | |
| bending strength | ISO 178 | 200 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.