Material Description
- Material Properties:High temperature resistance｜wear resistant
- Application Areas:Automotive components｜Special for cast film｜Application in the automotive field
- Color:--
- Grade:Optical grade
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO 75-2/B | 137 °C |
| 1.8MPa,未退火 | ISO 75-2/A | 123 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 6.5E-05 cm/cm/°C |
| TD | ISO 11359-2 | 6.6E-05 cm/cm/°C |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| shrinkage rate | 吸水率(饱和,23°C) | 0.24 % | |
| melt mass-flow rate | 300°C/1.2kg | ISO 1133 | 34 g/10min |
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 32.0 cm3/10min |
| shrinkage rate | TD:3.20mm | 0.50-0.70 % | |
| MD:3.20mm | 0.50-0.70 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| surface resistivity | IEC 60093 | 6E+15 ohms | |
| volume resistivity | IEC 60093 | 3E+16 ohms·cm | |
| dielectric strength | 1.00mm | IEC 60243-1 | 31 KV/mm |
| 3.00mm | IEC 60243-1 | 18 KV/mm | |
| relative permittivity | 100Hz | IEC 60250 | 3.10 |
| 1MHz | IEC 60250 | 3.10 | |
| Dissipation Factor | 100Hz | IEC 60250 | 6E-04 |
| 1MHz | IEC 60250 | 9E-03 | |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 2 |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile modulus | ISO 527-2 | 2400 Mpa | |
| tensile strength | 屈服 | ISO 527-2 | 63.0 Mpa |
| Tensile strain | 屈服 | ISO 527-2 | 5.8 % |
| Nominal tensile fracture strain | ISO 527-2 | 110 % | |
| flexural modulus | ISO 178 | 2300 Mpa | |
| bending strength | ISO 178 | 98.0 Mpa |
| impact performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | NoBreak |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.