Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | 内部方法 | 0.30-0.50 % | |
| Water absorption rate | ISO 62 | 1.3 % |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | ISO 2039-2 | 120 |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| elongation at break | ASTM D638/ISO 527 | 2.0 % | |
| tensile strength | ASTM D638/ISO 527 | 180 kg/cm²(MPa)[Lb/in²] | |
| Rockwell hardness | ASTM D785 | 120 | |
| Flexural modulus | ASTM D790/ISO 178 | 8.800 kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 260 kg/cm²(MPa)[Lb/in²] | |
| tensile strength | ISO 527-2 | 180 Mpa | |
| Tensile strain | ISO 527-2 | 3.0 % | |
| Flexural modulus | ISO 178 | 9500 Mpa | |
| bending strength | ISO 178 | 260 Mpa |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.38 | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 6 g/10min | |
| Water absorption rate | ASTM D570/ISO 62 | 1.25 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Volume resistivity | IEC 60093 | 1E+15 ohms·cm | |
| IEC 60250 | 3.80 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Combustibility (rate) | UL 94 | HB | |
| melting temperature | 220 ℃（℉） | ||
| Hot deformation temperature (HDT) | ISO 75-2/A | 210 °C | |
| melting temperature | ISO 11357-3 | 220 °C | |
| Hot deformation temperature (HDT) | ISO 75-2/B | 220 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.