PC/PBT XENOY™  1731J BK1066 SABIC INNOVATIVE SHANGHAI

301
  • Unit Price:US$ 2,713 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    106MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:Chemical resistance｜High impact resistance｜High mobility｜UV resistance
  • Application Areas:medical care｜Plastic bag｜Gears｜Automotive Applications
  • Color:--
  • Grade:Injection grade

Technical Data Sheet

impact performanceTest ConditionTest MethodTest Result
Charpy Notched Impact Strength23°CISO 179/1eA65 kJ/m²
Dart impact23°C,TotalEnergyASTM D376361.1 J
Dart impact-30°C,TotalEnergyASTM D376361.5 J
Impact strength of cantilever beam gap23°CISO 180/1A59 kJ/m²
Impact strength of cantilever beam gap-30°CISO 180/1A16 kJ/m²
flammabilityTest ConditionTest MethodTest Result
UL flame retardant rating1.5mmUL 94HB
mechanical propertiesTest ConditionTest MethodTest Result
Bending modulusISO 1782210 Mpa
bending strengthISO 17893.0 Mpa
bending strengthYield,50.0mmSpanASTM D79093.1 Mpa
Bending modulus50.0mmSpanASTM D7902340 Mpa
Tensile strainBreakISO 527-2/5090 %
elongationBreakASTM D638100 %
Tensile strainYieldISO 527-2/505.0 %
elongationYieldASTM D6385.0 %
tensile strengthBreakISO 527-2/5058.0 Mpa
Tensile modulusASTM D6382370 Mpa
Tensile modulusISO 527-2/12330 Mpa
tensile strengthYieldASTM D63861.4 Mpa
tensile strengthYieldISO 527-2/5060.0 Mpa
tensile strengthBreakASTM D63856.0 Mpa
thermal performanceTest ConditionTest MethodTest Result
Hot deformation temperature1.8MPa,Unannealed,6.40mmASTM D648107 °C
Hot deformation temperature1.8MPa,Unannealed,3.20mmASTM D64893.0 °C
Hot deformation temperature0.45MPa,Unannealed,6.40mmASTM D648116 °C
Linear coefficient of thermal expansionTD：-40to40°CISO 11359-27.6E-05 cm/cm/°C
Linear coefficient of thermal expansionTD：-40to40°CASTME8317.6E-05 cm/cm/°C
Linear coefficient of thermal expansionMD：-40to40°CISO 11359-27.8E-05 cm/cm/°C
Linear coefficient of thermal expansionMD：-40to95°CASTME8318.3E-05 cm/cm/°C
Linear coefficient of thermal expansionMD：-40to40°CASTME8317.8E-05 cm/cm/°C
Vicat softening temperature--ISO 306/B120130 °C
Vicat softening temperature--ISO 306/B50127 °C
Vicat softening temperatureASTM D152510125 °C
Hot deformation temperature1.8MPa,Unannealed,64.0mmSpanISO 75-2/Af99.0 °C
RTI ElecUL 74675.0 °C
RTI ImpUL 74675.0 °C
RTI StrUL 74675.0 °C
Physical propertiesTest ConditionTest MethodTest Result
melt mass-flow rate250°C/5.0kgISO 11338.0 g/10min
melt mass-flow rate250°C/5.0kgASTM D12389.6 g/10min
Specific volumeASTM D7920.820 cm³/g
Shrinkage rateMD：3.20mmInternal Method0.50-0.70 %
Shrinkage rateTD：3.20mmInternal Method0.60-0.80 %
Water absorption rateSaturation,23°CISO 620.28 %
Water absorption rateEquilibrium,23°C,50%RHISO 620.080 %
Electrical performanceTest ConditionTest MethodTest Result
High voltage arc tracing rateHVTRUL 746PLC 2
Hot wire ignitionHWIUL 746PLC 2
Arc resistanceASTM D495PLC 5
Compared to the anti leakage trace indexCTIUL 746PLC 2
High arc combustion indexHAIUL 746PLC 0
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.