ABS

ABS Toyolac® 700-314 TORAY MALAYSIA

654

Unit Price:US$ 1,688 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
57MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High gloss｜High mobility｜High temperature resistance｜Flame retardant
Application Areas:Automotive sector｜small home appliances｜Electronic field｜Electrical field｜Fitness equipment
Color:--
Grade:Impact resistant grade

Material Certification

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	23°C,12.7mm	ASTM D256	200 J/m
	Impact strength of cantilever beam gap	23°C,3.20mm	ASTM D256	220 J/m
		Impact strength of cantilever beam gap	0°C,12.7mm	ASTM D256	110 J/m
			Impact strength of cantilever beam gap	0°C,3.20mm	ASTM D256	160 J/m
				Impact strength of cantilever beam gap	-30°C,12.7mm	ASTM D256	80 J/m
				Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-30°C,3.20mm	ASTM D256	110 J/m
Charpy Notched Impact Strength	23°C	ISO 179/1eA	18 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating		UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
bending strength		ISO 178	77.0 Mpa
bending strength	bending strength		ASTM D790	73.0 Mpa
Bending modulus		ASTM D790	2300 Mpa
Tensile modulus		ISO 527-2/1	2600 Mpa
tensile strength	Yield	ASTM D638	46.0 Mpa
tensile strength	tensile strength	Yield	ISO 527-2/50	51.0 Mpa
elongation	Break	ASTM D638	15 %
Tensile strain	Break	ISO 527-2/50	>10 %

thermal performance	Test Condition	Test Method	Test Result
thermal conductivity		ASTMC177	0.16 W/m/K
Linear coefficient of thermal expansion	MD	ASTM D696	7.2E-05 cm/cm/°C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	81.0 °C
	Hot deformation temperature	1.8MPa,Unannealed,12.7mm	ASTM D648	92.0 °C
	Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	86.0 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	23°C,24hr	ASTM D570	0.30 %
Shrinkage rate	MD	ASTM D955	0.40-0.60 %
melt mass-flow rate	220°C/10.0kg	ISO 1133	40 g/10min
density		ISO 1183	1.04 g/cm³
density	density		ASTM D792	1.05 g/cm³

Electrical performance	Test Condition	Test Method	Test Result
Dielectric constant	1kHz	ASTM D150	3.10
Dielectric strength		ASTM D149	23 KV/mm
Volume resistivity	23°C	ASTM D257	>1.0E+16 ohms·cm
Surface resistivity		ASTM D257	>1.0E+16 ohms
Dissipation factor	1kHz	ASTM D150	6.2E-03

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Scale	ASTM D785	114

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

ABS Toyolac® 700-314 TORAY MALAYSIA

Material Description

Material Certification

Technical Data Sheet Compare

Technical Data Sheet