PBT

PBT VALOX™ DR51 SABIC INNOVATIVE US

281

Unit Price:US$ 3,308 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
65.8MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

For more details, please contact the supplier!

Material Description

Material Properties:Glass fiber reinforced｜Electrical performance
Application Areas:Non specific food｜Lawn equipment｜Garden equipment｜Industrial applications｜Automotive External Parts｜Electrical field｜Electronic field｜Architectural application field｜Outdoor applications｜Electrical appliances｜Engine hood parts｜Medical supplies｜Nursing supplies｜Plastic bag｜Automotive interior parts｜Casters｜Aerospace Applications
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	23°C	ASTM D256	53 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ASTM D4812	530 J/m

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.70mm	UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	Break	ASTM D638	93.1 Mpa
Tensile strain	Break	ASTM D638	5.0 %
Bending modulus	50.0mmSpan	ASTM D790	4830 Mpa
bending strength	Break,50.0mmSpan	ASTM D790	145 Mpa

thermal performance	Test Condition	Test Method	Test Result
RTI Str		UL 746	140 °C
RTI Elec		UL 746	130 °C
RTI Imp		UL 746	130 °C
Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	191 °C
Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	2.2E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：60to138°C	ASTME831	2.2E-05 cm/cm/°C
Hot deformation temperature	0.45MPa,Unannealed,6.40mm	ASTM D648	210 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	24hr	ASTM D570	0.070 %
Shrinkage rate	TD：--4	Internal Method	0.80-1.1 %
	Shrinkage rate	MD：--2	Internal Method	0.40-0.60 %
		Shrinkage rate	MD：--3	Internal Method	0.60-0.90 %
		Shrinkage rate	Shrinkage rate	TD：--2	Internal Method	0.50-0.80 %
density		ASTM D792	1.41 g/cm³
Specific volume		ASTM D792	0.712 cm³/g

Electrical performance	Test Condition	Test Method	Test Result
Dielectric constant	100Hz	ASTM D150	3.60
Dielectric strength	1.60mm,in Oil	ASTM D149	23 KV/mm
Dielectric strength	Dielectric strength	3.20mm,inAir	ASTM D149	20 KV/mm
Volume resistivity		ASTM D257	3.3E+16 ohms·cm
High voltage arc tracing rate	HVTR	UL 746	PLC 1
Dissipation factor	1MHz	ASTM D150	0.020
Arc resistance		ASTM D495	PLC 5
Compared to the anti leakage trace index	CTI	UL 746	PLC 2
Dielectric constant	1MHz	ASTM D150	3.40
Dissipation factor	100Hz	ASTM D150	2E-03

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Scale	ASTM D785	118

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.