PPS RYTON® R-4-02XT CPCHEM USA

470

Unit Price:US$ 10,656 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
26MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Glass fiber reinforced｜enhance｜Flame retardant｜High temperature resistance｜Filler: Glass fiber reinforced material｜40% filler by weight
Application Areas:Automotive sector｜Electrical appliances｜Application in the automotive field
Color:--
Grade:Flame retardant grade

Material Certification

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Suspended wall beam without notch impact strength		ISO 180	30 kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	3.18mm	ASTM D4812	510 J/m
Impact strength of cantilever beam gap		ISO 180/A	8.0 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	3.17mm	ASTM D256	80 J/m

flammability	Test Condition	Test Method	Test Result
Extreme Oxygen Index		ASTM D2863	53 %
UL flame retardant rating	1.6mm	UL 94	V-05VA

mechanical properties	Test Condition	Test Method	Test Result
compressive strength		ASTM D695	285 Mpa
bending strength		ISO 178	260 Mpa
Poisson's ratio			0.39
tensile strength		ASTM D638	179 Mpa
tensile strength	tensile strength		ISO 527-2	180 Mpa
elongation	Break	ASTM D638	1.5 %
Tensile strain	Break	ISO 527-2	1.4 %
Bending modulus		ASTM D790	14500 Mpa
Bending modulus	Bending modulus		ISO 178	14000 Mpa
bending strength		ASTM D790	255 Mpa

thermal performance	Test Condition	Test Method	Test Result
UL temperature rating		UL 746B	200to220 °C
Linear coefficient of thermal expansion	TD：导热系数	ASTME831	0.30 W/m/K
	Linear coefficient of thermal expansion	TD：100to200°C	ASTME831	9E-05 cm/cm/°C
		Linear coefficient of thermal expansion	TD：-50to50°C	ASTME831	4E-05 cm/cm/°C
			Linear coefficient of thermal expansion	MD：100to200°C	ASTME831	1.5E-05 cm/cm/°C
			Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：-50to50°C	ASTME831	2E-05 cm/cm/°C
Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	265 °C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	MD：3.20mm		0.20 %
Shrinkage rate	Shrinkage rate	TD：3.20mm		0.50 %
Water absorption rate	23°C,24hr	ASTM D570	0.020 %
density		ASTM D792	1.69 g/cm³

Electrical performance	Test Condition	Test Method	Test Result
Dielectric constant	25°C,1MHz	ASTM D150	3.90
Dielectric constant	Dielectric constant	25°C,1kHz	ASTM D150	3.80
Dielectric strength		ASTM D149	22 KV/mm
Volume resistivity		ASTM D257	1E+16 ohms·cm
insulation resistance	90°C		1E+11 ohms
Compared to the anti leakage trace index	CTI	UL 746	PLC 4
Arc resistance		ASTM D495	125 sec
Dissipation factor	25°C,1MHz	ASTM D150	3E-03
Dissipation factor	Dissipation factor	25°C,1kHz	ASTM D150	2E-03

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	M-Sale	ASTM D785	102
Rockwell hardness	Rockwell hardness	R-Sale	ASTM D785	120

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PPS RYTON® R-4-02XT CPCHEM USA

Material Description

Material Certification

Technical Data Sheet Compare

Technical Data Sheet