PPA AMODEL®  AS-1133HS NT SOLVAY USA

279
  • Unit Price:US$ 5,149 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    46MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:Filler: Glass fiber reinforced material｜33% filler by weight
  • Application Areas:Laptop case｜Valves/valve components｜Industrial applications｜Industrial components｜Metal substitution｜Lawn and garden equipment｜Power/Other Tools｜Oil/Gas Supplies｜currency｜Parts under the hood of a car｜Application in the automotive field｜Fuel pipeline｜Machine/mechanical components｜Vehicle electronics｜Shell｜Thick wall accessories (components)
  • Color:--
  • Grade:Injection grade

Technical Data Sheet

optical performanceTest ConditionTest MethodTest Result
transmissivity940nm:1.60mmASTM D1003>30 %
transmissivity1070nm:1.60mmASTM D1003>35 %
impact performanceTest ConditionTest MethodTest Result
Impact strength of simply supported beam without notchISO 179/1eU82 kJ/m²
flammabilityTest ConditionTest MethodTest Result
UL flame retardant rating3.2mmUL 94HB
mechanical propertiesTest ConditionTest MethodTest Result
Bending modulusISO 17810300 Mpa
bending strengthISO 178326 Mpa
bending strengthYieldASTM D790317 Mpa
Bending modulusASTM D79010300 Mpa
compressive strengthASTM D695276 Mpa
shear strengthASTM D732101 Mpa
Poisson's ratio7.58 0.41
Tensile modulusASTM D63813100 Mpa
Tensile modulusISO 527-212200 Mpa
tensile strengthYieldISO 527-2225 Mpa
tensile strengthBreakASTM D638221 Mpa
elongationBreakASTM D6382.5 %
Tensile strainBreakISO 527-23.0 %
thermal performanceTest ConditionTest MethodTest Result
Linear coefficient of thermal expansionTD：160to249°CASTME8311.3E-04 cm/cm/°C
Linear coefficient of thermal expansionTD：0to100°CASTME8315.9E-05 cm/cm/°C
Linear coefficient of thermal expansionMD：160to249°CASTME8311.4E-05 cm/cm/°C
Linear coefficient of thermal expansionMD：0to100°CASTME8312.3E-05 cm/cm/°C
Melting temperatureISO 11357-3310 °C
Melting temperatureASTM D3418310 °C
Continuous use temperature--3ASTM D3045185 °C
Continuous use temperature--2ASTM D3045164 °C
Hot deformation temperature1.8MPa,AnnealedISO 75-2/Af277 °C
Hot deformation temperature1.8MPa,Annealed,3.18mmASTM D648285 °C
Hot deformation temperature0.45MPa,Annealed,3.18mmASTM D648297 °C
Physical propertiesTest ConditionTest MethodTest Result
Shrinkage rateMDASTM D9550.40 %
Shrinkage rateTDASTM D9550.80 %
Water absorption rate24hrASTM D5700.21 %
Electrical performanceTest ConditionTest MethodTest Result
Dissipation factor1MHzASTM D1500.017
Dissipation factor60HzASTM D1505E-03
Dielectric constant1MHzASTM D1504.20
Dielectric constant60HzASTM D1504.40
Dielectric strength3.17mmASTM D14921 KV/mm
Volume resistivityASTM D2571E+16 ohms·cm
Compared to the anti leakage trace indexCTIUL 746 V
Arc resistanceASTM D495140 sec
hardnessTest ConditionTest MethodTest Result
Rockwell hardnessR-ScaleASTM D785125
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.