TPE Hytrel® 7246 DUPONT USA

375

Unit Price:US$ 5,204 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
57MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

For more details, please contact the supplier!

Material Description

Material Properties:Antichemical｜Aging resistance｜Thermal stability
Application Areas:Profile｜building materials｜Plate｜Casters｜film
Color:--
Grade:Extrusion grade

Material Certification

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result
density		ISO 1183	1.26 g/cm³
melt mass-flow rate		ISO 1133	13 g/10min
Melt volume flow rate		ISO 1133	12.0 cm3/10min
Shrinkage rate		ISO 294-4	1.6 %
Shrinkage rate	Shrinkage rate		ISO 294-4	1.6 %
Water absorption rate		ISO 62	0.30 %
	Water absorption rate		ISO 62	0.60 %
	Water absorption rate	Water absorption rate		ISO 62	0.20 %

hardness	Test Condition	Test Method	Test Result
Shore hardness		ISO 868	68
Shore hardness	Shore hardness		ISO 868	64

flammability	Test Method	Test Result
Limiting Oxygen Index	ISO 4589-2	23 %
burning rate	ISO 3795	DNI
UL flame retardant rating	UL 94,IEC60695-11-10,-20	HB

Supplementary Information	Test Condition	Test Method	Test Result
Emissions of Organic Compounds		VDA277	300 µgC/g

Filling analysis	Test Condition	Test Method	Test Result
Melt density			1.11 g/cm³
SpecificHeatCapacity of Melt			2150 J/kg/°C
ThermalConductivityofMelt			0.15 W/m/K

Impact resistance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap		ISO 8256/1	300 kJ/m²
Charpy Notched Impact Strength		ISO 179/1eA	7.0 kJ/m²
	Charpy Notched Impact Strength		ISO 179/1eA	8.0 kJ/m²
	Charpy Notched Impact Strength	Charpy Notched Impact Strength		ISO 179/1eA	36 kJ/m²
Impact strength of cantilever beam gap		ISO 180/1A	7.0 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		ISO 180/1A	38 kJ/m²

Mechanical properties	Test Condition	Test Method	Test Result
Tensile creep modulus		ISO 899-1	310 Mpa
Flexural modulus		ISO 178	550 Mpa
wear resistance		ISO 4649	100 mm³
Tensile modulus		ISO 527-2	550 Mpa
tensile strength		ISO 527-2	26.0 Mpa
	tensile strength		ISO 527-2	50.0 Mpa
		tensile strength		ISO 527-2	14.0 Mpa
			tensile strength		ISO 527-2	23.0 Mpa
			tensile strength	tensile strength		ISO 527-2	24.0 Mpa
Tensile strain		ISO 527-2	26 %
Tensile strain	Tensile strain		ISO 527-2	>300 %
Nominal tensile fracture strain		ISO 527-2	530 %
Tensile creep modulus		ISO 899-1	360 Mpa

elastomer	Test Condition	Test Method	Test Result
tear strength		ISO 34-1	170 kN/m
tear strength	tear strength		ISO 34-1	180 kN/m

Electrical performance	Test Condition	Test Method	Test Result
Surface Resistivity		IEC 60093	>1.0E+15 ohms
Volume resistivity		IEC 60093	2E+12 ohms·cm
dielectric strength		IEC 60243-1	20 KV/mm
relative permittivity		IEC 60250	4.00
relative permittivity	relative permittivity		IEC 60250	3.50
Dissipation Factor		IEC 60250	0.016
Dissipation Factor	Dissipation Factor		IEC 60250	0.030
Compared to the Leakage Tracking Index (CTI)		IEC 60112	PLC 0

Thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion		ISO 11359-2	8E-08 m²/s
Heat distortion temperature		ISO 75-2/B	100 °C
Heat distortion temperature	Heat distortion temperature		ISO 75-2/A	50.0 °C
brittle temperature		ISO 974	-97.0 °C
Glass Transition Temperature		ISO 11357-2	25.0 °C
vicat		ISO 306/A50	205 °C
vicat	vicat		ISO 306/B50	140 °C
melting temperature		ISO 11357-3	218 °C
Linear coefficient of thermal expansion		ISO 11359-2	1.8E-04 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion		ISO 11359-2	1.7E-04 cm/cm/°C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App