Material Description

Material Properties:High heat resistance｜Weather resistance
Application Areas:--
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	23°C	ISO 180/1A	12 kJ/m²
Charpy Notched Impact Strength	-30°C	ISO 179	6.0 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179	12 kJ/m²
Impact strength of cantilever beam gap	23°C,3.20mm	ASTM D256	200 J/m
	Impact strength of cantilever beam gap	23°C,6.40mm	ASTM D256	190 J/m
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-30°C	ISO 180/1A	5.0 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.5mm	UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	Yield	ASTM D638	46.0 Mpa
	tensile strength	Yield	ISO 527-2/50	47.0 Mpa
	tensile strength	tensile strength	Break	ISO 527-2/50	34.0 Mpa
elongation	Break	ASTM D638	55 %
Tensile strain	Break	ISO 527-2/50	20 %
Bending modulus		ASTM D790	2260 Mpa
Bending modulus	Bending modulus		ISO 178	2100 Mpa
bending strength		ASTM D790	66.3 Mpa
bending strength	bending strength		ISO 178	67.0 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	86.0 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Annealed	ISO 75-2/A	105 °C
Vicat softening temperature		ASTM D15256	113 °C
	Vicat softening temperature	--	ISO 306/A50	112 °C
	Vicat softening temperature	Vicat softening temperature	--	ISO 306/B50	100 °C
Linear coefficient of thermal expansion	MD	ISO 11359-2	9.1E-05 cm/cm/°C
Hot deformation temperature	Annealed	ASTM D648	103 °C
Hot deformation temperature	Hot deformation temperature	Unannealed	ASTM D648	93 °C

Physical properties	Test Condition	Test Method	Test Result
density	比重	ASTM D792	1.07 g/cm³
density	density	23°C	ISO 1183	1.07 g/cm³
melt mass-flow rate	220°C/10.0kg	ASTM D1238	13 g/10min
Melt Volume Flow Rate (MVR)	220°C/10.0kg	ISO 1133	12.0 cm3/10min
Shrinkage rate		ISO 294-4	0.40-0.70 %

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Scale	ASTM D785	105

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

ASA KIBILAC® PW-978W TAIWAN CHIMEI

Material Description

Technical Data Sheet Compare

Technical Data Sheet