ASA GELOY™ HRA222F-10000 SABIC INNOVATIVE SHANGHAI
336
- Unit Price:US$ 4,113 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:79MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:High temperature resistance｜Thermal stability
- Application Areas:Home appliance components｜Lawn garden equipment
- Color:--
- Grade:Flame retardant grade
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45 MPa, 未退火, 4.00 mm, 100 mm 跨距 | ISO 75-2/Be | 99.0 °C |
| 1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距 | ISO 75-2/Ae | 88.0 °C | |
| vicat | -- | ISO 306/A50 | 111 °C |
| -- | ISO 306/B50 | 102 °C | |
| -- | ISO 306/B120 | 104 °C | |
| ball-indentation hardness | 73 到 77°C | IEC 60695-10-2 | 通过 |
| Linear coefficient of thermal expansion | 流动 : -30 到 80°C | ISO 11359-2 | 6.9E-5 cm/cm/°C |
| 横向 : -30 到 80°C | ISO 11359-2 | 7.1E-5 cm/cm/°C | |
| 横向 : 23 到 80°C | ISO 11359-2 | 7.5E-5 cm/cm/°C | |
| RTI Elec | UL 746 | 90.0 °C | |
| RTI Imp | UL 746 | 90.0 °C | |
| RTI | UL 746 | 90.0 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 2.0 mm | UL 94 | V-0 |
| Limiting Oxygen Index | ISO 4589-2 | 29 % |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Melt volume flow rate | 260°C/2.16 kg | ISO 1133 | 13.0 cm3/10min |
| shrinkage rate | Flow | 内部方法 | 0.40 - 0.60 % |
| Water absorption rate | 饱和, 23°C | ISO 62 | 0.60 % |
| 平衡, 23°C, 50% RH | ISO 62 | 0.20 % | |
| Outdoor applicability | UL 746C | f1 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 0 | |
| IEC 60112 | PLC 0 |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 80 to 90 °C | ||
| drying time | 2.0 to 4.0 hr | ||
| Suggested maximum moisture content | 0.020 % | ||
| Hopper temperature | 60 to 80 °C | ||
| Temperature at the rear of the barrel | 200 to 230 °C | ||
| Temperature in the middle of the barrel | 220 to 260 °C | ||
| Temperature at the front of the material cylinder | 230 to 270 °C | ||
| Spray nozzle temperature | 220 to 260 °C | ||
| Processing (melt) temperature | 230 to 270 °C | ||
| mold temperature | 50 to 70 °C |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | --3 | ASTM D638 | 2590 Mpa |
| -- | ISO 527-2/1 | 2520 Mpa | |
| tensile strength | 屈服4 | ASTM D638 | 63.0 Mpa |
| 屈服5 | ASTM D638 | 59.0 Mpa | |
| 屈服 | ISO 527-2/5 | 62.0 Mpa | |
| 屈服 | ISO 527-2/50 | 60.0 Mpa | |
| 断裂5 | ASTM D638 | 66.0 Mpa | |
| 断裂4 | ASTM D638 | 56.0 Mpa | |
| 断裂 | ISO 527-2/5 | 51.0 Mpa | |
| 断裂 | ISO 527-2/50 | 45.0 Mpa | |
| elongation | 屈服5 | ASTM D638 | 4.2 % |
| 屈服4 | ASTM D638 | 4.3 % | |
| 屈服 | ISO 527-2/5 | 4.3 % | |
| 屈服 | ISO 527-2/50 | 4.4 % | |
| 断裂5 | ASTM D638 | > 100 % | |
| 断裂4 | ASTM D638 | > 100 % | |
| 断裂 | ISO 527-2/5 | > 50 % | |
| flexural modulus | ISO 178 | 2510 Mpa | |
| bending strength | ISO 178 | 93.0 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.