mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Wear factor	0.49MPa,0.30m/sec5	JISK7218	100	10^-8mm³/N·m
	Wear factor	0.060MPa,0.15m/sec6	JISK7218	200	10^-8mm³/N·m
	Wear factor	Wear factor	0.060MPa,0.15m/sec7	JISK7218	200	10^-8mm³/N·m
Tensile modulus		ISO 527-2	1700	Mpa
tensile strength		ISO 527-2	45.0	Mpa
Nominal tensile fracture strain		ISO 527-2	50	%
Bending modulus		ISO 178	1550	Mpa
bending strength		ISO 178	57.0	Mpa
Friction coefficient	Dynamic2	JISK7218	0.65
Friction coefficient	Friction coefficient	Steel - Dynamic3	JISK7218	0.30
Wear factor	0.49MPa,0.30m/sec4	JISK7218	<1.0	10^-8mm³/N·m
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	MD：23to55°C	Internal Method	1.2E-04	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：23to55°C	Internal Method	1.3E-04	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	TD:2.00mm	ISO 294-4	1.6	%
Shrinkage rate	Shrinkage rate	MD:2.00mm	ISO 294-4	1.8	%
melt mass-flow rate	190°C/2.16kg	ISO 1133	8.0	g/10min
Melt Volume Flow Rate (MVR)	190°C/2.16kg	ISO 1133	7.00	cm3/10min
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Surface resistivity		IEC 60093	8E+13	ohms
Volume resistivity		IEC 60093	2E+13	ohms·cm
Supplementary Information	Test Condition	Test Method	Test Result	Test Unit
ColourNumber			CF2001

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.