'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
POM Delrin® 100ST DuPont, European Union
112
- Unit Price:US$ 10,360 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:20MT
- Delivery Terms:FOB
- Port of Loading :Shenzhen Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
- Material Comparison:
Transaction Guarantee:
Supplier Information
Dongguan East Asia Plastic Co., Ltd.
+86 755 ********View
serv********View
+86 ********View
For more details, please contact the supplier!
Material Description
- Material Properties:High impact resistance｜wear resistant｜Toughening
- Application Areas:Fitness equipment
- Color:--
- Grade:Injection grade
Material Certification
Technical Data Sheet
| impact performance | Test Condition | Test Method | Test Result | Test Unit |
|---|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 18 | kJ/m² |
| 23°C | ISO 179/1eA | 90 | kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | NoBreak | |
| 23°C | ISO 179/1eU | NoBreak | ||
| Impact strength of cantilever beam gap | -40°C | ISO 180/1A | 20 | kJ/m² |
| 23°C | ISO 180/1A | 90 | kJ/m² | |
| flammability | Test Condition | Test Method | Test Result | Test Unit |
| FMVSS flammability | FMVSS302 | B | ||
| Flammability level | 1.5mm | IEC 60695-11-10,-20 | HB | |
| UL flame retardant rating | 1.5mm | UL 94 | HB | |
| Burning rate | 1.00mm | ISO 3795 | 41 | mm/min |
| mechanical properties | Test Condition | Test Method | Test Result | Test Unit |
| bending strength | 3.5%Strain | ISO 178 | 34.0 | Mpa |
| Bending modulus | ISO 178 | 1100 | Mpa | |
| Tensile creep modulus | 1000hr | ISO 899-1 | 550 | Mpa |
| 1hr | ISO 899-1 | 1100 | Mpa | |
| Nominal tensile fracture strain | ISO 527-2 | >50 | % | |
| Tensile strain | Yield | ISO 527-2 | 30 | % |
| tensile strength | Yield | ISO 527-2 | 41.0 | Mpa |
| Tensile modulus | ISO 527-2 | 1400 | Mpa | |
| Friction coefficient | vs.Itself-Dynamic,1hr | ASTM D1894 | 0.32 | |
| thermal performance | Test Condition | Test Method | Test Result | Test Unit |
| Glass transition temperature | ISO 11357-2 | -35.0 | °C | |
| Melting temperature | ISO 11357-3 | 178 | °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1.3E-04 | cm/cm/°C |
| TD | ISO 11359-2 | 1.4E-04 | cm/cm/°C | |
| Hot deformation temperature | 1.8MPa,Unannealed | ISO 75-2/A | 60.0 | °C |
| AnnealingTemperature | 160 | °C | ||
| AnnealingTime-Optional | 30.0 | min/mm | ||
| Effective thermal diffusivity coefficient | 6E-08 | m²/s | ||
| Hot deformation temperature | 0.45MPa,Unannealed | ISO 75-2/B | 100 | °C |
| Physical properties | Test Condition | Test Method | Test Result | Test Unit |
| Shrinkage rate | MD | ISO 294-4 | 1.3 | % |
| TD | ISO 294-4 | 1.4 | % | |
| Melt Volume Flow Rate (MVR) | 190°C/2.16kg | ISO 1133 | 1.70 | cm3/10min |
| melt mass-flow rate | ISO 1133 | 2.0 | g/10min | |
| density | ISO 1183 | 1.34 | g/cm³ | |
| Water absorption rate | Equilibrium,23°C,2.00mm,50%RH | ISO 62 | 0.35 | % |
| Saturation,23°C,2.00mm | ISO 62 | 0.90 | % | |
| MediumDensity | 1.14 | g/cm³ | ||
| Electrical performance | Test Condition | Test Method | Test Result | Test Unit |
| Compared to the anti leakage trace index | IEC 60112 | PLC 0 | ||
| Relative permittivity | 1MHz | IEC 60250 | 3.80 | |
| 100Hz | IEC 60250 | 4.40 | ||
| Surface resistivity | IEC 60093 | 1E+14 | ohms | |
| Volume resistivity | IEC 60093 | 1E+14 | ohms·cm | |
| hardness | Test Condition | Test Method | Test Result | Test Unit |
| Rockwell hardness | M-Sale | ISO 2039-2 | 58 | |
| R-Sale | ISO 2039-2 | 105 | ||
| Supplementary Information | Test Condition | Test Method | Test Result | Test Unit |
| Emission | VDA275 | <8.00 | mg/kg | |
| EmissionofOrganicCompounds | VDA277 | 2.90 | µgC/g | |
| SpecificWear-Against | ASTM D1894 | 60.0 | 10^-6mm³/N·m |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.