PC Makrolon® 9125 901510 COVESTRO GERMANY

208

Unit Price:US$ 3,542 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Medium viscosity｜Flame retardant｜Easy to demould｜Filler: Glass fiber reinforced material｜20% filler by weight｜20% filler by weight
Application Areas:Casters
Color:--
Grade:Enhanced level

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	23°C,CompleteBreak	ISO 7391	8.0 kJ/m²
Impact strength of simply supported beam without notch	-30°C,Complete Break	ISO 179/1eU	45 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C,Complete Break	ISO 179/1eU	40 kJ/m²
Impact strength of cantilever beam gap	23°C,CompleteBreak	ISO 7391	8.0 kJ/m²
Multi axis Instrumented Impact Energy	-30°C	ISO 6603-2	5.00 J
Multi axis Instrumented Impact Energy	Multi axis Instrumented Impact Energy	23°C	ISO 6603-2	5.00 J
Multi axis Instrumented Peak Impact Force	-30°C	ISO 6603-2	800 N
Multi axis Instrumented Peak Impact Force	Multi axis Instrumented Peak Impact Force	23°C	ISO 6603-2	800 N

flammability	Test Condition	Test Method	Test Result
SelfIgnition		ASTM D1929	550 °C
Needle flame test	MethodK:3.00mm	IEC 60695-11-5	2.0 min
	Needle flame test	MethodK:2.00mm	IEC 60695-11-5	2.0 min
		Needle flame test	MethodK:1.50mm	IEC 60695-11-5	1.0 min
			Needle flame test	MethodF:3.00mm	IEC 60695-11-5	2.0 min
				Needle flame test	MethodF:2.00mm	IEC 60695-11-5	2.0 min
				Needle flame test	Needle flame test	MethodF:1.50mm	IEC 60695-11-5	2.0 min
FlashIgnitionTemperature		ASTM D1929	470 °C
Burning rate - US-FMVSS	>1.00mm	ISO 3795	passed
UL flame retardant rating	0.36mm	UL 94	V-2
UL flame retardant rating	UL flame retardant rating	1.5mm	UL 94	V-0
Burning wire flammability index	1.5mm	IEC 60695-2-12	960 °C
Burning wire flammability index	Burning wire flammability index	3.0mm	IEC 60695-2-12	960 °C
Hot filament ignition temperature	1.5mm	IEC 60695-2-13	850 °C
Hot filament ignition temperature	Hot filament ignition temperature	3.0mm	IEC 60695-2-13	850 °C
Extreme Oxygen Index		ISO 4589-2	35 %
Small flame combustion test	2.00mm	DIN 4102	B2
Small flame combustion test	Small flame combustion test	MethodKandF:2.00mm	DIN 53438-1,-3	K1.F1

mechanical properties	Test Condition	Test Method	Test Result
Bending modulus	23°C	ISO 178	5600 Mpa
Tensile creep modulus	1000hr	ISO 899-1	5200 Mpa
Tensile creep modulus	Tensile creep modulus	1hr	ISO 899-1	5700 Mpa
Tensile strain	Break,23°C	ISO 527-2/5	2.5 %
tensile strength	Break,23°C	ISO 527-2/5	85.0 Mpa
Tensile modulus	23°C	ISO 527-2/1	5800 Mpa
bending strength	23°C	ISO 178	140 Mpa
Bending strain	23°C	ISO 178	3.0 %

thermal performance	Test Condition	Test Method	Test Result
RTI Imp	1.5mm	UL 746	125 °C
RTI Str	1.5mm	UL 746	125 °C
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	142 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	138 °C
thermal conductivity	23°C	ISO 8302	0.23 W/m/K
RTI Elec	1.5mm	UL 746	130 °C
Vicat softening temperature	--	ISO 306/B50	145 °C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	146 °C
Ball Pressure Test	136°C	IEC 60695-10-2	Pass
Linear coefficient of thermal expansion	MD：23to55°C	ISO 11359-2	3E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：23to55°C	ISO 11359-2	6.5E-05 cm/cm/°C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.10 %
Water absorption rate	Water absorption rate	Saturation,23°C	ISO 62	0.24 %
Shrinkage rate	MD:2.00mm3	ISO 294-4	0.35 %
	Shrinkage rate	TD:2.00mm3	ISO 294-4	0.45 %
		Shrinkage rate	MD	ISO 2577	0.30-0.50 %
		Shrinkage rate	Shrinkage rate	TD	ISO 2577	0.30-0.50 %
Melt Volume Flow Rate (MVR)	300°C/1.2kg	ISO 1133	8.00 cm3/10min
melt mass-flow rate	300°C/1.2kg	ISO 1133	10 g/10min
Apparent density		ISO 60	0.64 g/cm³
density	23°C	ISO 1183	1.34 g/cm³

Electrical performance	Test Condition	Test Method	Test Result
Surface resistivity		IEC 60093	1E+16 ohms
Volume resistivity	23°C	IEC 60093	1E+16 ohms·cm
Dielectric strength	23°C,1.00mm	IEC 60243-1	36 KV/mm
Relative permittivity	23°C,100Hz	IEC 60250	3.30
Relative permittivity	Relative permittivity	23°C,1MHz	IEC 60250	3.30
Dissipation factor	23°C,100Hz	IEC 60250	1E-03
Dissipation factor	Dissipation factor	23°C,1MHz	IEC 60250	9E-03
Compared to the anti leakage trace index	SolutionA	IEC 60112	V
Compared to the anti leakage trace index	Compared to the anti leakage trace index	SolutionB	IEC 60112	V

hardness	Test Condition	Test Method	Test Result
Ball Pressure Test		ISO 2039-1	148 Mpa

Supplementary Information	Test Condition	Test Method	Test Result
Electrolytic corrosion	23°C	IEC 60426	A1

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PC Makrolon® 9125 901510 COVESTRO GERMANY

Material Description

Technical Data Sheet Compare

Technical Data Sheet