PBT DURANEX® 531HS JAPAN POLYPLASTIC
178
- Unit Price:US$ 2,909 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Thermal shock resistance｜Hydrolysis resistance
- Application Areas:Electrical applications｜Electronic and electrical components
- Color:--
- Grade:--
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | M级 | ISO 2039-2 | 75 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 1.8Mpa | ISO 75-1/-2 | 208 °C |
| Linear coefficient of thermal expansion | 流动方向 | ISO 11359-2 | 2 ×10-5/℃ |
| 垂直方向 | ISO 11359-2 | 13 ×10-5/℃ | |
| UL flame retardant rating | UL 94 | HB | |
| Heat Deflection Temperature | 1.8MPa,未退火 | ISO 75-2/A | 208 °C |
| Linear coefficient of thermal expansion | MD：23到55°C | 内部方法 | 2E-05 cm/cm/°C |
| TD：23to55°C | 内部方法 | 9E-05 cm/cm/°C | |
| Combustibility (rate) | UL 94 | HB | |
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | 2 mm/mm.℃ |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ColorNumber | ED3002 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| volume resistivity | IEC 60093 | 1×1016 Ω.cm | |
| dielectric strength | 3.00mm | IEC 60243-1 | 16 KV/mm |
| volume resistivity | IEC 60093 | 1E+16 ohms·cm | |
| ASTM D257/IEC 60093 | 1.0 x 10^16 Ω.cm |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Water absorption rate | 23°C,24hr | ISO 62 | 0.20 % |
| density | ASTM D792/ISO 1183 | 1.47 |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | 10.8 kJ/m² | |
| tensile strength | ISO 527-1/-2 | 118 Mpa | |
| bending strength | ISO 178 | 230 Mpa | |
| flexural modulus | ISO 178 | 8100 Mpa | |
| tensile strength | ISO 527-2 | 118 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 2.7 % |
| flexural modulus | ISO 178 | 8100 Mpa | |
| bending strength | ISO 178 | 187 Mpa | |
| tensile strength | ASTM D638/ISO 527 | 118 kg/cm²(MPa)[Lb/in²] | |
| flexural modulus | ASTM D790/ISO 178 | 8100 kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 187 kg/cm²(MPa)[Lb/in²] | |
| Elongation at break | ASTM D638/ISO 527 | 2.7 % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.