PC INFINO® CF-3300 BK Samsung Cheil South Korea

171

Unit Price:US$ 2,866 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High rigidity｜Antichemical｜Filler: Glass fiber reinforced material｜Filler: Glass fiber reinforced material
Application Areas:Phone｜Electronic and Electrical Applications
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	23°C	ISO 180/1A	17 kJ/m²
	Impact strength of cantilever beam gap	23°C,6.35mm	ASTM D256	150 J/m
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C,3.18mm	ASTM D256	180 J/m
Charpy Notched Impact Strength	23°C	ISO 179/1eA	18 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.8mm	UL 94	V-2
UL flame retardant rating	UL flame retardant rating	3.2mm	UL 94	V-1

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	Yield	ISO 527-2/50	125 Mpa
tensile strength	tensile strength	Yield	ASTM D638	120 Mpa
Tensile modulus		ISO 527-2/50	6900 Mpa
Tensile modulus	Tensile modulus		ASTM D638	6400 Mpa
bending strength		ISO 178	180 Mpa
bending strength	bending strength		ASTM D790	170 Mpa
Bending modulus		ISO 178	7300 Mpa
Bending modulus	Bending modulus		ASTM D790	6500 Mpa
Tensile strain	Break	ISO 527-2/50	3.8 %
elongation	Break	ASTM D638	3.8 %
tensile strength	Break	ISO 527-2/50	125 Mpa
tensile strength	tensile strength	Break	ASTM D638	120 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Unannealed,6.40mm	ASTM D648	143 °C
	Hot deformation temperature	0.45MPa,Unannealed,4.00mm	ISO 75-2/B	143 °C
		Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	140 °C
		Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,4.00mm	ISO 75-2/A	138 °C
Vicat softening temperature	--	ISO 306/B50	147 °C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	148 °C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	MD:3.20mm	ISO 2577	0.10-0.30 %
	Shrinkage rate	TD:3.20mm	ISO 2577	0.10-0.30 %
		Shrinkage rate	TD：3.20mm	ASTM D955	0.10-0.30 %
		Shrinkage rate	Shrinkage rate	MD：3.20mm	ASTM D955	0.10-0.30 %
melt mass-flow rate	250°C/10.0kg	ISO 1133	22 g/10min
melt mass-flow rate	melt mass-flow rate	250°C/10.0kg	ASTM D1238	22 g/10min
density		ASTM D792	1.40 g/cm³
density	density		ISO 1183	1.40 g/cm³

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Scale	ISO 2039-2	115
Rockwell hardness	Rockwell hardness	R-Scale	ASTM D785	115

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PC INFINO® CF-3300 BK Samsung Cheil South Korea

Material Description

Technical Data Sheet Compare

Technical Data Sheet