PBT Cristin® S600F20-NC010 DUPONT USA
239
- Unit Price:US$ 4,425 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:74MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Flame retardant｜Glass fiber reinforced｜Good dimensional stability｜Good resistance to chemical corrosion
- Application Areas:Electronic and electrical components｜Automotive Applications｜Industrial applications｜Automotive Applications
- Color:--
- Grade:Injection grade
Material Certification
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melting temperature | ISO 3146 | 225 ℃ | |
| Linear coefficient of thermal expansion | 平行流动方向，23 to 55°C (73 to 130°F) | ISO 11359-1 | 0.00013 cm/cm/°C |
| 垂直流动方向，23 to 55°C (73 to 130°F) | ISO 11359-1 | 0.00013 cm/cm/°C | |
| Heat Deflection Temperature | 0.45 Mpa，未退火 | ISO 75B-1 | 180 ℃ |
| 1.8 Mpa，未退火 | ISO 75B-1 | 60 ℃ | |
| UL flame retardant rating | 1.50 mm | UL94 | HB |
| 3.00 mm | UL94 | HB | |
| Linear coefficient of thermal expansion | MD：-40to23°C | ISO 11359-2 | 8E-05 cm/cm/°C |
| MD：55to160°C | ISO 11359-2 | 1.9E-04 cm/cm/°C | |
| TD：-- | ISO 11359-2 | 1.2E-04 cm/cm/°C | |
| TD：-40to23°C | ISO 11359-2 | 9E-05 cm/cm/°C | |
| TD：55to160°C | ISO 11359-2 | 2E-04 cm/cm/°C | |
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO 75-2/B | 115 °C |
| 0.45MPa,退火 | ISO 75-2/B | 180 °C | |
| 1.8MPa,未退火 | ISO 75-2/A | 50.0 °C | |
| 1.8MPa,退火 | ISO 75-2/A | 60.0 °C | |
| Glass Transition Temperature | ISO 11357-2 | 55.0 °C | |
| vicat | ISO 306/B50 | 175 °C | |
| melting temperature | ISO 11357-3 | 225 °C | |
| PeakCrystallizationTemperature | ISO 11357-3 | 192 °C | |
| Linear coefficient of thermal expansion | MD：-- | ISO 11359-2 | 1.1E-04 cm/cm/°C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL 94 | HB |
| 1.5mm | UL 94 | HB | |
| 0.75mm | IEC 60695-11-10,-20 | HB | |
| 1.5mm | IEC 60695-11-10,-20 | HB | |
| Limiting Oxygen Index | ISO 4589-2 | 22 % | |
| FMVSS flammability | FMVSS302 | SE | |
| Fogging-G-value | condensate | ISO 6452 | 0.0 g |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Odor | VDA270 | 3.00 | |
| Thermal Desorption Analysis of Organic Emissions | VDA278 | 1.00 µg/g |
| Other performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Limiting Oxygen Index | ISO 4589-1 | 22 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 4.0 kJ/m² |
| 23°C | ISO 179/1eA | 5.0 kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | NoBreak |
| 23°C | ISO 179/1eU | NoBreak | |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 4.5 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | NoBreak |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Water absorption rate | 23C/59RH | ISO 62 | 0.2 % |
| Sat/23C | ISO 62 | 0.40 % | |
| shrinkage rate | Across Flow | ISO 294-4 | 1.6 % |
| Flow | ISO 294-4 | 1.7 % | |
| density | ISO 1183 | 1.31 g/cm | |
| MediumDensity | 1.11 g/cm³ | ||
| Ejection Temperature | 170 °C | ||
| SpecificHeatCapacity of Melt | 2110 J/kg/°C | ||
| ThermalConductivityofMelt | 0.21 W/m/K | ||
| density | ISO 1183 | 1.31 g/cm³ | |
| melt mass-flow rate | 250°C/2.16kg | ISO 1133 | 19 g/10min |
| shrinkage rate | TD | ISO 294-4 | 1.6 % |
| MD | ISO 294-4 | 1.7 % | |
| Water absorption rate | 饱和,23°C,2.00mm | ISO 62 | 0.40 % |
| 平衡,23°C,2.00mm,50%RH | ISO 62 | 0.20 % | |
| viscosity number | ISO 307 | 130 cm³/g |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Dissipation Factor | 100Hz | IEC 60250 | 7.9E-04 |
| 1MHz | IEC 60250 | 0.020 | |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 1 | |
| Surface Resistivity | IEC 60093 | 1E+12 ohms | |
| volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| dielectric strength | IEC 60243-1 | 26 KV/mm | |
| relative permittivity | 100Hz | IEC 60250 | 3.60 |
| 1MHz | IEC 60250 | 3.20 |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23 ℃, Type 1, Edgewise | ISO 179 | No Break KJ/m |
| Charpy Notched Impact Strength | -30 ℃, Type 1, Edgewise, Notch A | ISO 179 | 4 KJ/m |
| 23 ℃, Type 1, Edgewise, Notch A | ISO 179 | 4.5 KJ/m | |
| Impact strength of cantilever beam gap | 23 ℃, Type 1, Notch A | ISO 180 | 4 KJ/m |
| Tensile stress | 23 ℃, 50 mm/min，屈服 | ISO 527-1 | 58 MPa |
| elongation | 23 ℃, 50 mm/min，屈服 | ISO 527-1 | 7.6 % |
| Nominal fracture strain | 23 ℃, 50 mm/min | ISO 527-1 | 40 % |
| Tensile creep modulus | 1000h | ISO 899-1 | 1800 MPa |
| Tensile modulus | 23 ℃, 1.0 mm/min | ISO 527-1 | 2600 MPa |
| bending strength | ISO 178 | 85 MPa | |
| Impact strength of simply supported beam without notch | -30 ℃, Type 1, Edgewise | ISO 179 | No Break KJ/m |
| Nominal tensile fracture strain | ISO 527-2 | 40 % | |
| Tensile creep modulus | 1hr | ISO 899-1 | 2600 Mpa |
| 1000hr | ISO 899-1 | 1800 Mpa | |
| flexural modulus | ISO 178 | 2200 Mpa | |
| bending strength | ISO 178 | 85.0 Mpa | |
| Tensile modulus | ISO 527-2 | 2500 Mpa | |
| tensile strength | 屈服 | ISO 527-2 | 58.0 Mpa |
| Tensile strain | 屈服 | ISO 527-2 | 5.0 % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.