PC Makrolon® LED-2245 COVESTRO GERMANY
331
- Unit Price:US$ 3,789 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:91.8MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:High temperature resistance｜High mobility｜Flame retardant｜Antichemical｜transparent
- Application Areas:Automotive sector｜Casters｜Electronic field｜Electrical field｜lens｜Lighting applications｜Optical applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ball-indentation hardness | ISO 2039-1 | 115 Mpa |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| RTI Str | 1.5mm | UL 746 | 125 °C |
| RTI Imp | 1.5mm | UL 746 | 115 °C |
| RTI Elec | 1.5mm | UL 746 | 125 °C |
| Linear coefficient of thermal expansion | TD：23to55°C | ISO 11359-2 | 6.5E-05 cm/cm/°C |
| thermal conductivity | 23°C | ISO 8302 | 0.20 W/m/K |
| Linear coefficient of thermal expansion | MD：23到55°C | ISO 11359-2 | 6.5E-05 cm/cm/°C |
| ball-indentation hardness | 136°C | IEC 60695-10-2 | Pass |
| vicat | -- | ISO 306/B120 | 146 °C |
| Glass Transition Temperature | ISO 11357-2 | 145 °C | |
| vicat | -- | ISO 306/B50 | 145 °C |
| Heat Deflection Temperature | 1.8MPa,未退火 | ISO 75-2/A | 125 °C |
| 0.45MPa,未退火 | ISO 75-2/B | 138 °C |
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Haze ratio | 3000µm | ISO 14782 | <0.50 % |
| transmissivity | 4000µm | ISO 13468-2 | >89.0 % |
| 3000µm | ISO 13468-2 | >89.0 % | |
| 2000µm | ISO 13468-2 | 90.0 % | |
| 1000µm | ISO 13468-2 | 90.0 % | |
| refractive index | ISO 489 | 1.584 |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Burning rate - US-FMVSS | >1.00mm | ISO 3795 | passed |
| Hot filament ignition temperature | 3.0mm | IEC 60695-2-13 | 900 °C |
| Limiting Oxygen Index | ISO 4589-2 | 28 % | |
| Hot filament ignition temperature | 1.5mm | IEC 60695-2-13 | 875 °C |
| 0.75mm | IEC 60695-2-13 | 875 °C | |
| Burning wire flammability index | 3.0mm | IEC 60695-2-12 | 930 °C |
| 1.0mm | IEC 60695-2-12 | 850 °C | |
| 1.5mm | IEC 60695-2-12 | 875 °C | |
| UL flame retardant rating | 0.75mm | UL 94 | V-2 |
| 2.9mm | UL 94 | HB | |
| SelfIgnitionTemperature | ASTM D1929 | 550 °C | |
| FlashIgnitionTemperature | ASTM D1929 | 480 °C |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C,局部断裂 | ISO 7391 | 60 kJ/m² |
| -30°C,完全断裂 | ISO 7391 | 12 kJ/m² | |
| Impact strength of simply supported beam without notch | -60°C | ISO 179/1eU | NoBreak |
| Multi axis Instrumented Peak Impact Force | -30°C | ISO 6603-2 | 5900 N |
| 23°C | ISO 6603-2 | 4900 N | |
| Impact strength of cantilever beam gap | 23°C,局部断裂 | ISO 7391 | 55 kJ/m² |
| Multi axis Instrumented Impact Energy | -30°C | ISO 6603-2 | 60.0 J |
| 23°C | ISO 6603-2 | 55.0 J | |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | NoBreak |
| Impact strength of cantilever beam gap | -30°C,完全断裂 | ISO 7391 | 12 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | NoBreak |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| relative permittivity | 23°C,100Hz | IEC 60250 | 3.10 |
| dielectric strength | 23°C,1.00mm | IEC 60243-1 | 34 KV/mm |
| Surface Resistivity | IEC 60093 | 1E+16 ohms | |
| volume resistivity | 23°C | IEC 60093 | 1E+16 ohms·cm |
| Compared to the Leakage Tracking Index (CTI) | 解决方案B | IEC 60112 | PLC 4 |
| 解决方案A | IEC 60112 | PLC 2 | |
| Dissipation Factor | 23°C,1MHz | IEC 60250 | 9.5E-03 |
| relative permittivity | 23°C,1MHz | IEC 60250 | 3.00 |
| Dissipation Factor | 23°C,100Hz | IEC 60250 | 5E-04 |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.12 % |
| shrinkage rate | MD:2.00mm | ISO 294-4 | 0.65 % |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.30 % |
| shrinkage rate | TD:2.00mm | ISO 294-4 | 0.70 % |
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 34.0 cm3/10min |
| Apparent density | ISO 60 | 0.66 g/cm³ | |
| density | 23°C | ISO 1183 | 1.19 g/cm³ |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile strain | 屈服,23°C | ISO 527-2/50 | 6.0 % |
| Tensile modulus | 23°C | ISO 527-2/1 | 2350 Mpa |
| tensile strength | 屈服,23°C | ISO 527-2/50 | 63.0 Mpa |
| 断裂,23°C | ISO 527-2/50 | 60.0 Mpa | |
| bending strength | 23°C | ISO 178 | 97.0 Mpa |
| 3.5%Strain,23°C | ISO 178 | 73.0 Mpa | |
| flexural modulus | 23°C | ISO 178 | 2350 Mpa |
| Tensile strain | 断裂,23°C | ISO 527-2/50 | 130 % |
| Nominal tensile fracture strain | 23°C | ISO 527-2/50 | >50 % |
| Bending Strain | 23°C | ISO 178 | 7.1 % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.