Material Properties:Flame retardant｜Glass fiber reinforced｜high strength｜High temperature resistance｜Filler: Glass fiber reinforced material｜40% filler by weight
Application Areas:Bottle cap｜household electrical appliances｜Casters｜Electrical applications｜Automotive Applications｜Fitness equipment｜Application in the automotive field
Color:--
Grade:Extrusion grade

Material Certification

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of cantilever beam gap	3.17mm	ASTM D256	80	J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		ISO 180/A	8.0	kJ/m²
Suspended wall beam without notch impact strength	3.18mm	ASTM D4812	530	J/m
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength		ISO 180	35	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.6mm	UL 94	V-05VA
Extreme Oxygen Index		ASTM D2863	57	%
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
tensile strength		ASTM D638	179	Mpa
tensile strength	tensile strength		ISO 527-2	185	Mpa
elongation	Break	ASTM D638	1.5	%
Tensile strain	Break	ISO 527-2	1.5	%
Bending modulus		ASTM D790	14500	Mpa
Bending modulus	Bending modulus		ISO 178	14000	Mpa
bending strength		ASTM D790	255	Mpa
bending strength	bending strength		ISO 178	260	Mpa
compressive strength		ASTM D695	275	Mpa
Poisson's ratio		ISO 527	0.40
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	265	°C
Linear coefficient of thermal expansion	MD：-50to50°C	ASTME831	1.5E-05	cm/cm/°C
	Linear coefficient of thermal expansion	MD：100to200°C	ASTME831	1E-05	cm/cm/°C
		Linear coefficient of thermal expansion	TD：-50to50°C	ASTME831	4E-05	cm/cm/°C
			Linear coefficient of thermal expansion	TD：100to200°C	ASTME831	8.5E-05	cm/cm/°C
			Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：导热系数	ASTME831	0.33	W/m/K
UL temperature rating		UL 746B	200to220	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ASTM D792	1.68	g/cm³
Shrinkage rate	MD：3.20mm		0.20	%
Shrinkage rate	Shrinkage rate	TD：3.20mm		0.50	%
Water absorption rate	23°C,24hr	ASTM D570	0.020	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Surface resistivity		ASTM D257	1E+16	ohms
Volume resistivity		ASTM D257	1E+16	ohms·cm
Dielectric strength		ASTM D149	22	KV/mm
Dielectric constant	25°C,1kHz	ASTM D150	3.90
Dielectric constant	Dielectric constant	25°C,1MHz	ASTM D150	3.80
Dissipation factor	25°C,1kHz	ASTM D150	2E-03
Dissipation factor	Dissipation factor	25°C,1MHz	ASTM D150	2E-03
Arc resistance		ASTM D495	125	sec
Compared to the anti leakage trace index	CTI	UL 746	PLC 4
insulation resistance	90°C		1E+11	ohms
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	M-Sale	ASTM D785	100
Rockwell hardness	Rockwell hardness	R-Sale	ASTM D785	120

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.