PC/PBT XENOY™ 1731J-1001 SABIC INNOVATIVE US
259
- Unit Price:US$ 2,769 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:133MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Chemical resistance｜High impact resistance｜High mobility｜UV resistance
- Application Areas:medical care｜Plastic bag｜Gears｜Automotive Applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 1.8MPa,Unannealed,64.0mmSpan | ISO 75-2/Af | 99.0 °C |
| vicat | ASTM D152510 | 125 °C | |
| -- | ISO 306/B50 | 127 °C | |
| -- | ISO 306/B120 | 130 °C | |
| Linear coefficient of thermal expansion | MD：-40to40°C | ASTME831 | 7.8E-05 cm/cm/°C |
| MD：-40到95°C | ASTME831 | 8.3E-05 cm/cm/°C | |
| MD：-40到40°C | ISO 11359-2 | 7.8E-05 cm/cm/°C | |
| TD：-40到40°C | ASTME831 | 7.6E-05 cm/cm/°C | |
| TD：-40到40°C | ISO 11359-2 | 7.6E-05 cm/cm/°C | |
| Heat Deflection Temperature | 0.45MPa,未退火,6.40mm | ASTM D648 | 116 °C |
| 1.8MPa,未退火,3.20mm | ASTM D648 | 93.0 °C | |
| 1.8MPa,未退火,6.40mm | ASTM D648 | 107 °C | |
| RTI Elec | UL 746 | 75.0 °C | |
| RTI Imp | UL 746 | 75.0 °C | |
| RTI Str | UL 746 | 75.0 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 16 kJ/m² |
| 23°C | ISO 180/1A | 59 kJ/m² | |
| Dart impact | -30°C,TotalEnergy | ASTM D3763 | 61.5 J |
| 23°C,TotalEnergy | ASTM D3763 | 61.1 J | |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 65 kJ/m² |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Specific volume | ASTM D792 | 0.820 cm³/g | |
| melt mass-flow rate | 250°C/5.0kg | ASTM D1238 | 9.6 g/10min |
| 250°C/5.0kg | ISO 1133 | 8.0 g/10min | |
| shrinkage rate | MD：3.20mm | 内部方法 | 0.50-0.70 % |
| TD：3.20mm | 内部方法 | 0.60-0.80 % | |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.28 % |
| 平衡,23°C,50%RH | ISO 62 | 0.080 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| arc resistance | ASTM D495 | PLC 5 | |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 2 |
| High arc combustion index (HAI) | HAI | UL 746 | PLC 0 |
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 2 |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 2 |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | 断裂 | ISO 527-2/50 | 58.0 Mpa |
| elongation | 屈服 | ASTM D638 | 5.0 % |
| Tensile strain | 屈服 | ISO 527-2/50 | 5.0 % |
| elongation | 断裂 | ASTM D638 | 100 % |
| Tensile strain | 断裂 | ISO 527-2/50 | 90 % |
| flexural modulus | 50.0mm跨距 | ASTM D790 | 2340 Mpa |
| ISO 178 | 2210 Mpa | ||
| bending strength | ISO 178 | 93.0 Mpa | |
| 屈服,50.0mm跨距 | ASTM D790 | 93.1 Mpa | |
| Tensile modulus | ASTM D638 | 2370 Mpa | |
| ISO 527-2/1 | 2330 Mpa | ||
| tensile strength | 屈服 | ASTM D638 | 61.4 Mpa |
| 屈服 | ISO 527-2/50 | 60.0 Mpa | |
| 断裂 | ASTM D638 | 56.0 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.