PA66

PA66 Zytel® 70G30HSL SV320A DUPONT USA

219

Unit Price:US$ 3,567 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
51MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Thermal stability
Application Areas:sporting goods｜Electrical applications
Color:--
Grade:--

Technical Data Sheet

Filling analysis	Test Method	Test Result
Melt density		1.21 g/cm³
Specific Heat Capacity of Melt		2290 J/kg/°C
Thermal Conductivity of Melt		0.21 W/m/K
Emission of Organic Compounds	VDA 277	6.00 µgC/g
Odor	VDA 270	4.50

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	60 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	80 kJ/m²

flammability	Test Condition	Test Method	Test Result
Burning rate	1.00 mm	ISO 3795	24 mm/min
UL flame retardant rating		UL 94	HB
UL flame retardant rating	UL flame retardant rating		UL 94	HB
Extreme Oxygen Index		ISO 4589-2	24 %
FMVSS combustion rate		FMVSS 302	SE/B
Atomization	F-value (refraction)	ISO 6452	95 %
Atomization	Atomization	G-value (condensate)	ISO 6452	3.0E-4 g

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO 527-2	9800 Mpa
tensile strength	Break	ISO 527-2	195 Mpa
Tensile strain	Break	ISO 527-2	3.5 %

injection	Test Condition	Test Result
drying temperature		80 °C
Drying time - hot air dryer		2.0 to 4.0 hr
Maximum Screw Tangential Speed		12 m/min
Hold Pressure Time		3.00 s/mm
Maintain pressure	Drying Recommended	yes
Maintain pressure	Maintain pressure		50.0 to 100 Mpa
Mold Temperature, Optimum		100 °C
Mold temperature		70 to 120 °C
Melt Temperature, Optimum		295 °C
Processing (melt) temperature		285 to 305 °C
Suggested maximum moisture content		0.20 %

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	260 °C
Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	253 °C
Glass transition temperature		ISO 11357-2	80.0 °C
Melting temperature		ISO 11357-3	262 °C
Linear coefficient of thermal expansion	Flow	ISO 11359-2	2.8E-5 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow	ISO 11359-2	9.5E-5 cm/cm/°C
Effective thermal diffusivity coefficient			6.85E-8 m²/s

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	横向Flow	ISO 294-4	1.1 %
Shrinkage rate	Shrinkage rate	Flow	ISO 294-4	0.30 %
Water absorption rate	Saturation, 23°C, 2.00 mm	ISO 62	6.9 %
Water absorption rate	Water absorption rate	Equilibrium, 23°C, 2.00 mm, 50% RH	ISO 62	2.0 %

Electrical performance	Test Condition	Test Method	Test Result
Surface resistivity		IEC 62631-3-2	-- ohms
Volume resistivity		IEC 62631-3-1	1.0E+11 ohms·m
Dissipation factor	100 Hz	IEC 62631-2-1	0.016
Dissipation factor	Dissipation factor	1 MHz	IEC 62631-2-1	0.016
Compared to the anti leakage trace index	3.00 mm	UL 746	PLC 0
Compared to the anti leakage trace index	Compared to the anti leakage trace index		IEC 60112	V

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PA66 Zytel® 70G30HSL SV320A DUPONT USA

Material Description

Technical Data Sheet Compare

Technical Data Sheet