LCP SUMIKASUPER® E6007LHF SUMITOMO JAPAN
350
- Unit Price:US$ 7,566 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:122MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Low warpage｜Good forming performance｜Glass fiber reinforced｜enhance
- Application Areas:Automotive sector
- Color:--
- Grade:Extrusion grade
Material Certification
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | ASTM D785 | 106 |
| other | Test Condition | Test Method | Test Result |
|---|---|---|---|
| characteristic | 低翘曲性 耐磨性能良好 低粘度 流动性高 刚性高 耐化学性良好 | ||
| purpose | 电气 电子应用领域 连接器 线圈骨架 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | ASTM D648/ISO 75 | 269 ℃（℉） | |
| ASTM D648 | 269 °C | ||
| Linear coefficient of thermal expansion | 内部方法 | 2.0E-6 cm/cm/°C | |
| 内部方法 | 8.5E-5 cm/cm/°C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-0 | |
| Limiting Oxygen Index | ISO 527-1 | 40 % | |
| Solder resistance | 内部方法 | 300 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Elongation at break | ASTM D638/ISO 527 | 5.1 % | |
| flexural modulus | ASTM D790/ISO 178 | 11800 kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 158 kg/cm²(MPa)[Lb/in²] | |
| tensile strength | ASTM D638 | 157 Mpa | |
| elongation | ASTM D638 | 5.1 % | |
| flexural modulus | ASTM D790 | 11800 Mpa | |
| bending strength | ASTM D790 | 158 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Suspended wall beam without notch impact strength | ASTM D256 | 250 J/m |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.67 | |
| Water absorption rate | ASTM D570/ISO 62 | 0.020 % | |
| shrinkage rate | 内部方法 | 0.60 % | |
| 内部方法 | 0.20 % | ||
| Water absorption rate | ASTM D570 | 0.020 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| volume resistivity | ASTM D257 | 1.0E+15 ohms·cm | |
| dielectric constant | ASTM D150 | 3.80 | |
| ASTM D150 | 3.50 | ||
| Dissipation Factor | ASTM D150 | 0.026 | |
| ASTM D150 | 4.0E-3 | ||
| arc resistance | ASTM D495 | 124 sec | |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 3 |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 130 °C | ||
| drying time | 4.0 to 24 hr | ||
| Temperature at the rear of the barrel | 280 to 320 °C | ||
| Temperature in the middle of the barrel | 320 to 340 °C | ||
| Temperature at the front of the material cylinder | 340 to 360 °C | ||
| Spray nozzle temperature | 340 to 360 °C | ||
| Processing (melt) temperature | 350 °C | ||
| mold temperature | 40 to 160 °C | ||
| Injection Pressure | 80.0 to 160 Mpa | ||
| injection speed | 中等偏快 | ||
| pressure holding | 20.0 to 40.0 Mpa | ||
| Back pressure | 1.00 to 5.00 Mpa | ||
| screw speed | 50 to 100 rpm |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.