PA66 Zytel® 80G33L DUPONT USA

236

Unit Price:US$ 5,631 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details
Material Comparison:
PA66 Zytel® 80G33L DUPONT CANADA

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

For more details, please contact the supplier!

Material Description

Material Properties:Thermal stability｜Glass fiber reinforced
Application Areas:Automotive sector｜Electronic field｜Electrical field
Color:--
Grade:Enhanced level

Material Certification

Technical Data Sheet Compare

thermal performance	Test Condition	Test Method	Test Result
Heat Deflection Temperature	0.45 MPa, 未退火	ISO 75-2/B	262 °C
Heat Deflection Temperature	Heat Deflection Temperature	1.8 MPa, 未退火	ISO 75-2/A	247 °C
melting temperature		ISO 11357-3	262 °C
Linear coefficient of thermal expansion	流动	ISO 11359-2	1.5E-5 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	横向	ISO 11359-2	1.2E-4 cm/cm/°C
Effective thermal diffusivity coefficient			8.50E-8 m²/s

flammability	Test Condition	Test Method	Test Result
burning rate	1.00 mm	ISO 3795	23 mm/min
UL flame retardant rating		UL 94	HB
UL flame retardant rating	UL flame retardant rating		UL 94	HB
Limiting Oxygen Index		ISO 4589-2	23 %
FMVSS combustion rate		FMVSS 302	SE/B
雾化 - G-value (condensate)		ISO 6452	8.0E-4 g

Impact resistance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	80 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	91 kJ/m²
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	80 kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C	ISO 180/1U	74 kJ/m²

Filling analysis	Test Method	Test Result
Melt density		1.12 g/cm³
Ejection Temperature		210 °C
Specific Heat Capacity of Melt		2200 J/kg/°C
Thermal Conductivity of Melt		0.22 W/m/K
Emission of Organic Compounds	VDA 277	25.0 µgC/g
Odor	VDA 270	3.00

Physical properties	Test Condition	Test Method	Test Result
shrinkage rate	横向流量	ISO 294-4	0.80 %
shrinkage rate	shrinkage rate	流量	ISO 294-4	0.30 %
Water absorption rate	24 hr, 23°C	ISO 62	0.83 %
	Water absorption rate	饱和, 23°C, 2.00 mm	ISO 62	4.5 %
	Water absorption rate	Water absorption rate	平衡, 23°C, 2.00 mm, 50% RH	ISO 62	1.5 %

Electrical performance	Test Condition	Test Method	Test Result
Compared to the Leakage Tracking Index (CTI)		IEC 60112	V

injection	Test Condition	Test Method	Test Result
drying temperature			80 °C
Drying time - hot air dryer			2.0 to 4.0 hr
Suggested maximum moisture content			0.20 %
Processing (melt) temperature			285 to 305 °C
Melt Temperature, Optimum			295 °C
mold temperature			50 to 100 °C
Mold Temperature, Optimum			80 °C
pressure holding			50.0 to 100 Mpa
pressure holding	pressure holding	Drying Recommended		yes
Hold Pressure Time			3.00 s/mm
Maximum Screw Tangential Speed			12 m/min

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO 527-2	8700 Mpa
tensile strength	断裂	ISO 527-2	142 Mpa
Tensile strain	断裂	ISO 527-2	4.0 %
flexural modulus		ISO 178	7400 Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.