ASA

ASA GELOY™  CR7520 GY6C348 SABIC INNOVATIVE US

303
  • Unit Price:US$ 2,235 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    31MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:High impact resistance｜High temperature resistance｜High mobility
  • Application Areas:Automotive sector
  • Color:--
  • Grade:Injection grade

Technical Data Sheet

optical performanceTest ConditionTest MethodTest Result
gloss60°,无织构ASTM D52395
impact performanceTest ConditionTest MethodTest Result
Dart impact-30°C,TotalEnergyASTM D376320.0 J
Dart impact23°C,TotalEnergyASTM D376335.0 J
Impact strength of cantilever beam gap23°CISO 180/1A19 kJ/m²
Impact strength of cantilever beam gap-30°CISO 180/1A4.5 kJ/m²
Impact strength of cantilever beam gap23°CASTM D256320 J/m
Impact strength of cantilever beam gap-30°CASTM D25659 J/m
Charpy Notched Impact Strength23°CISO 179/1eA17 kJ/m²
flammabilityTest ConditionTest MethodTest Result
UL flame retardant rating1.5mmUL 94HB
mechanical propertiesTest ConditionTest MethodTest Result
bending strengthYield,50.0mmSpanASTM D79058.6 Mpa
Bending modulusISO 1782000 Mpa
Bending modulus50.0mmSpanASTM D7901790 Mpa
Tensile strainBreakISO 527-2/5044 %
elongationBreakASTM D63840 %
Tensile strainYieldISO 527-2/503.1 %
tensile strengthYieldASTM D63841.4 Mpa
Tensile modulusISO 527-2/12000 Mpa
Tensile modulusASTM D6381790 Mpa
tensile strengthBreakISO 527-2/5029.0 Mpa
tensile strengthBreakASTM D63834.5 Mpa
tensile strengthYieldISO 527-2/5039.0 Mpa
thermal performanceTest ConditionTest MethodTest Result
Hot deformation temperature0.45MPa,Unannealed,3.20mmASTM D64887.8 °C
Hot deformation temperature0.45MPa,Unannealed,6.40mmASTM D64890.6 °C
Hot deformation temperature0.45MPa,Unannealed,64.0mmSpanISO 75-2/Bf91.0 °C
Hot deformation temperature1.8MPa,Unannealed,3.20mmASTM D64876.7 °C
RTI ImpUL 74650.0 °C
RTI StrUL 74650.0 °C
Linear coefficient of thermal expansionMD：-30to0°CASTME8318.5E-05 cm/cm/°C
Linear coefficient of thermal expansionMD：-40to40°CASTME8318.6E-05 cm/cm/°C
Linear coefficient of thermal expansionMD：0to100°CASTME8319E-05 cm/cm/°C
Linear coefficient of thermal expansionTD：-40to40°CASTME8319.2E-05 cm/cm/°C
Hot deformation temperature1.8MPa,Unannealed,6.40mmASTM D64879.4 °C
Hot deformation temperature1.8MPa,Unannealed,64.0mmSpanISO 75-2/Af80.0 °C
Hot deformation temperature1.8MPa,AnnealedASTM D64895.6 °C
RTI ElecUL 74650.0 °C
Vicat softening temperatureASTM D1525999.4 °C
Vicat softening temperatureISO 306/B5090.0 °C
Physical propertiesTest ConditionTest MethodTest Result
melt mass-flow rate260°C/5.0kgASTM D123813 g/10min
melt mass-flow rate220°C/10.0kgASTM D12387.0 g/10min
densityASTM D7921.06 g/cm³
Outdoor applicabilityUL 746Cf2
Water absorption rateEquilibrium,23°CASTM D5700.55 %
Shrinkage rateMD：3.20mmInternal Method0.50-0.70 %
melt mass-flow rate280°C/3.8kgASTM D123820 g/10min
Electrical performanceTest ConditionTest MethodTest Result
High arc combustion indexHAIUL 746PLC 0
Hot wire ignitionHWIUL 746PLC 3
Compared to the anti leakage trace indexCTIUL 746PLC 0
Surface resistivityASTM D257>1.0E+15 ohms
Dielectric strength3.20mm,inOilASTM D14916 KV/mm
Dielectric constant50HzASTM D1505.20
Dielectric constant60HzASTM D1505.20
Dielectric constant1MHzASTM D1503.21
Dissipation factor50HzASTM D1500.15
Dissipation factor60HzASTM D1500.15
Dissipation factor1MHzASTM D1500.026
hardnessTest ConditionTest MethodTest Result
Rockwell hardnessR-ScaleASTM D78586
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.