PC/ABS Bayblend® FR3000 701133 COVESTRO GERMANY

226

Unit Price:US$ 3,542 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Flame retardant｜UV resistance｜High mobility
Application Areas:Electrical field｜Electronic field｜Household appliances｜Household appliances｜Automotive sector
Color:--
Grade:Flame retardant grade

Material Certification

Technical Data Sheet

Filling analysis	Test Condition	Test Method	Test Result
Melt viscosity	240°C	ISO 11443-A	150 Pa·s
ISO			PC+ABS-FR(40)

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	23°C	ISO 180/A	30 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.5 mm	UL 94	V-0
UL flame retardant rating	UL flame retardant rating	2.0 mm	UL 94	5VB
Extreme Oxygen Index		ISO 4589-2	34 %

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus	23°C	ISO 527-2/1	2650 Mpa
tensile strength	Yield, 23°C	ISO 527-2/50	64.0 Mpa
Tensile strain	Yield, 23°C	ISO 527-2/50	3.9 %
Nominal tensile fracture strain	23°C	ISO 527-2/50	40 %

injection	Test Condition	Test Method	Test Result
Drying Temperature - Dry Air Dryer			80 °C
Drying time - Dry Air Dryer			4.0 hr
Suggested maximum moisture content			< 0.020 %
Suggested injection volume			30 to 70 %
Temperature at the rear of the barrel			220 to 230 °C
Temperature in the middle of the barrel			225 to 235 °C
Temperature at the front of the material cylinder			230 to 240 °C
Spray nozzle temperature			255 to 265 °C
Processing (melt) temperature			240 to 270 °C
Mold temperature			60 to 90 °C
Back pressure			5.00 to 15.0 Mpa
Exhaust hole depth			0.025 to 0.075 mm

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	95.0 °C
Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	85.0 °C
Vicat softening temperature		ISO 306/B120	103 °C

Physical properties	Test Condition	Test Method	Test Result
density	23°C	ISO 1183	1.18 g/cm³
Melt Volume Flow Rate (MVR)	240°C/5.0 kg	ISO 1133	20.0 cm3/10min
Shrinkage rate	横向Flow	ISO 2577	0.40 - 0.60 %
Shrinkage rate	Shrinkage rate	Flow	ISO 2577	0.40 - 0.60 %
Water absorption rate	Saturation, 23°C	ISO 62	0.40 %
Water absorption rate	Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.10 %

Electrical performance	Test Condition	Test Method	Test Result
Surface resistivity		IEC 60093	1.0E+16 ohms
Volume resistivity	23°C	IEC 60093	1.0E+16 ohms·cm
Relative permittivity	23°C, 100 Hz	IEC 60250	3.00
Relative permittivity	Relative permittivity	23°C, 1 MHz	IEC 60250	2.90

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PC/ABS Bayblend® FR3000 701133 COVESTRO GERMANY

Material Description

Material Certification

Technical Data Sheet Compare

Technical Data Sheet