PPS LNP™ KONDUIT™ OX11315 BK SABIC INNOVATIVE US

334

Unit Price:US$ 8,200 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
63MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Carbon fiber reinforced｜High impact resistance
Application Areas:Automotive Applications
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Multi axis Instrumented Impact Energy		ISO 6603-2	1.14	J
Dart impact	23°C,TotalEnergy	ASTM D3763	5.14	J
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	3.9	kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180/1A	1.7	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	2.5mm	UL 94	5VA
UL flame retardant rating	UL flame retardant rating	1.0mm	UL 94	V-0
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Bending modulus		ISO 178	21400	Mpa
bending strength		ISO 178	84.0	Mpa
bending strength	bending strength	Break,50.0mmSpan	ASTM D790	82.0	Mpa
Bending modulus	50.0mmSpan	ASTM D790	26500	Mpa
Tensile strain	Break	ISO 527-2/5	0.30	%
elongation	Break	ASTM D638	0.20	%
tensile strength	Break	ISO 527-2/5	54.0	Mpa
tensile strength	tensile strength	Break	ASTM D638	41.0	Mpa
Tensile modulus		ISO 527-2/1	18400	Mpa
Tensile modulus	Tensile modulus		ASTM D638	30100	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
RTI Str		UL 746	130	°C
RTI Imp		UL 746	130	°C
RTI Elec		UL 746	130	°C
thermal conductivity	--9	ASTM D790/ISO 178	15	W/m/K
thermal conductivity	thermal conductivity	--8	ASTM D790/ISO 178	3.5	W/m/K
specific heat		ASTMC351	1260	J/kg/°C
Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	238	°C
	Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	242	°C
		Hot deformation temperature	0.45MPa,Unannealed,64.0mmSpan	ISO 75-2/Bf	275	°C
		Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	275	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	MD：24hr	ASTM D955	0.34	%
Shrinkage rate	Shrinkage rate	TD：24hr	ASTM D955	0.44	%
Water absorption rate	24hr,50%RH	ASTM D570	0.010	%
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	<0.010	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Surface resistivity		ASTM D257	2.4E+15	ohms

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

PPS LNP™ KONDUIT™ OX11315 BK SABIC INNOVATIVE US

Material Description

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index