ABS POLYLAC® PA-718 TAIWAN CHIMEI

458

Unit Price:US$ 3,350 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
40MT
Delivery Terms:
FOB
Port of Loading :
Kaoshiung port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High impact resistance｜High gloss
Application Areas:small home appliances｜Electronic field｜Electrical field
Color:--
Grade:Injection grade

Technical Data Sheet

other	Test Condition	Test Method	Test Result	Test Unit
characteristic			注塑、高光泽、高硬度ABS.钢琴拷漆
purpose			电视机外框等
Basic Performance	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate		ASTM D-1238	1.6	g/10min
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength	1/4＂ 2.8mm/min	ASTM D-790	720(10200)	kg/cm2(lb/in2)
Bending modulus	1/4＂ 2.8mm/min	ASTM D-790	25000(350000)	kg/cm2(lb/in2)
Impact strength of cantilever beam gap	1/4＂ 23℃	ASTM D-256	10(1.8)	kg·cm/cm(ft-lb/in)
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	1/8 ＂23℃	ASTM D-256	12(2.2)	kg·cm/cm(ft-lb/in)
Shore hardness	1/2＂	ASTM D-785	114	R scale
tensile strength	1/8＂ 6mm/min	ASTM D-638	480(6800)	kg/cm2(lb/in2)
elongation	1/8＂ 6mm/min	ASTM D-638	30	%
tensile strength		ASTM D638/ISO 527	480(6800)	kg/cm²(MPa)[Lb/in²]
elongation		ASTM D638/ISO 527	30	%
Bending modulus		ASTM D790/ISO 178	25000(350000)	kg/cm²(MPa)[Lb/in²]
bending strength		ASTM D790/ISO 178	720(10200)	kg/cm²(MPa)[Lb/in²]
Impact strength of cantilever beam gap		ASTM D256/ISO 179	10(1.8)	kg·cm/cm(J/M)ft·lb/in
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		ASTM D256/ISO 179	12(2.2)	kg·cm/cm(J/M)ft·lb/in
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Vicat softening temperature	1/8＂，50℃/hr	ASTM D-1525	103(217)	℃（℉）
Hot deformation temperature	1/4＂，120℃/hr	ASTM D-648	98(208)	℃（℉）
Hot deformation temperature	Hot deformation temperature	1/4＂，120℃/hr	ASTM D-648	86(186)	℃（℉）
Burning rate		UL -94	1/16＂HB
Pencil hardness	Load 765g	ASTM D-3363	H+
Combustibility (rate)		UL 94	1/16＂HB
Hot deformation temperature	HDT	ASTM D648/ISO 75	98(208)	℃（℉）
Hot deformation temperature	Hot deformation temperature	HDT	ASTM D648/ISO 75	86(186)	℃（℉）
Vicat softening temperature		ASTM D1525/ISO R306	103(217)	℃（℉）
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ASTM D792/ISO 1183	1.125
melt mass-flow rate		ASTM D1238/ISO 1133	1.6	g/10min

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

ABS POLYLAC® PA-718 TAIWAN CHIMEI

Material Description

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index