PA66

PA66 RADILON® A RV200K RADICI SUZHOU

247

Unit Price:US$ 4,673 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
19.5MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:--
Application Areas:--
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	45 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	40 kJ/m²

flammability	Test Condition	Test Method	Test Result
flammability		FMVSS 302	0 mm/min
Burning wire flammability index	2.0 mm	IEC 60695-2-12	700 °C
UL flame retardant rating	0.8 mm	UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
bending strength		ISO 178	210 Mpa
Bending modulus		ISO 178	6300 Mpa
Tensile strain	Break	ISO 527-2/1A/5	3.0 %
tensile strength	Break	ISO 527-2/1A/5	140 Mpa
Tensile modulus		ISO 527-2/1A/1	6900 Mpa

injection	Test Condition	Test Method	Test Result
Processing (melt) temperature			280 to 300 °C
Mold temperature			80 to 100 °C
Injection speed			中等偏快
Suggested maximum moisture content			0.15 %
Dew Point - Hot Air Drying Machine			-20 °C
Drying time - hot air dryer			2.0 to 4.0 hr
Drying temperature - hot air dryer			80 °C

thermal performance	Test Condition	Test Method	Test Result
Melting temperature		ISO 11357-3	260 °C
Vicat softening temperature		ISO 306/B50	240 °C
Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/Af	220 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Equilibrium, 23°C, 2.00 mm, 50% RH	ISO 62	2.1 %
Water absorption rate	Water absorption rate	Saturation, 23°C, 2.00 mm	ISO 62	7.8 %
Shrinkage rate	Flow	ISO 294-4	0.40 %
Shrinkage rate	Shrinkage rate	横向Flow	ISO 294-4	0.90 %

Electrical performance	Test Condition	Test Method	Test Result
Compared to the anti leakage trace index	Solution A	IEC 60112	PLC 1
Volume resistivity		IEC 60093	1.0E+15 ohms·cm
Surface resistivity		IEC 60093	1.0E+12 ohms

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.