PBT 3300-2 CELANESE USA
234
- Unit Price:US$ 3,732 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:21MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Glass fiber reinforced｜30% enhancement
- Application Areas:Automotive sector
- Color:--
- Grade:Enhanced level
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45Mpa | ISO 75-1/-2 | 225 °C |
| 8.0Mpa | ISO 75-1/-2 | 150 °C | |
| vicat | ISO 306 | 220 °C | |
| Linear coefficient of thermal expansion | 横向 | ISO 11359-2 | 1 E-4/℃ |
| Limiting Oxygen Index | ISO 4589 | 20 % | |
| UL flame retardant rating | UL 94 | HB | |
| Glass Transition Temperature | ISO 11357-1 | 60 °C | |
| Heat Deflection Temperature | 1.8Mpa | ISO 75-1/-2 | 205 °C |
| Linear coefficient of thermal expansion | 纵向 | ISO 11359-2 | 0.25 E-4/℃ |
| melting temperature | ISO 11357-1 | 225 °C |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO 1183 | 1530 kg/m | |
| Melt volume flow rate | ISO 1133 | 17 CM | |
| shrinkage rate | 纵向 | ISO 294-4 | 0.3-0.5 % |
| Water absorption rate | 23℃,饱和 | ISO 62 | 0.4 % |
| 23℃,50%相对湿度 | ISO 62 | 0.2 % | |
| shrinkage rate | 横向 | ISO 294-4 | 0.7-0.9 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| volume resistivity | 100Hz | IEC 6250 | 4.5 |
| 1MHz | IEC 60250 | 4.1 | |
| Dielectric dissipation factor | 100Hz | IEC 60250 | 22 E-4 |
| 1MHz | IEC 60250 | 160 E-4 | |
| volume resistivity | IEC 60093 | ＞1E13 ohm.m | |
| Surface Resistivity | IEC 60093 | ＞1E15 Ohm | |
| dielectric strength | IEC 60243-1 | 31 KV/mm | |
| Compared to the Leakage Traceability Index (CTI) | IEC 60112 | 425 |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | 1mm/min | ISO 527-2/1A | 9200 Mpa |
| tensile strength | 5mm/min | ISO 527-2/1A | 130 Mpa |
| Elongation at break | 5mm/min | ISO 527-2/1A | 2.5 % |
| flexural modulus | 23℃ | ISO 178 | 9700 Mpa |
| bending strength | 23℃ | ISO 178 | 210 Mpa |
| Charpy Notched Impact Strength | 23℃ | ISO 179/1eU | 46 KJ/m |
| -30℃ | ISO 179/1eU | 45 KJ/m | |
| 23℃ | ISO 179/1eA | 8.5 KJ/m | |
| -30℃ | ISO 179/1eA | 8.5 KJ/m | |
| Rockwell hardness | ISO 2039-2 | 90 M | |
| Impact strength of cantilever beam gap | 23℃ | ISO 180/1A | 7.5 KJ/m |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.