Material Properties:High temperature resistance｜Filler: Glass mineral｜70% filler by weight
Application Areas:Automotive components
Color:--
Grade:Injection grade

Technical Data Sheet Compare

hardness	Test Condition	Test Method	Test Result
Rockwell hardness		ISO 2039-2	93

thermal performance	Test Condition	Test Method	Test Result
Heat Deflection Temperature		ISO 75-2/A	272 °C
Linear coefficient of thermal expansion		ISO 11359-2	1.9E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion		ISO 11359-2	2E-05 cm/cm/°C

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating		UL 94	V-0

Supplementary Information	Test Condition	Test Method	Test Result
Flowability2		内部方法	9.10 CM

Mechanical properties	Test Method	Test Result
tensile strength	ISO 527-2	89.0 Mpa
Tensile strain	ISO 527-2	0.70 %
flexural modulus	ISO 178	19100 Mpa
bending strength	ISO 178	161 Mpa

Impact resistance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch		ISO 179	5.7 kJ/m²

Electrical performance	Test Condition	Test Method	Test Result
dielectric constant		IEC 60250	6.50
Dissipation Factor		IEC 60250	0.023
volume resistivity		ASTM D257	1E+16 ohms·cm
dielectric strength		IEC 60243-1	13 KV/mm
dielectric strength	dielectric strength		IEC 60243-1	14 KV/mm

Physical properties	Test Condition	Test Method	Test Result
density		ISO 1183	2.10 g/cm³
shrinkage rate		ISO 294-4	0.60 %
shrinkage rate	shrinkage rate		ISO 294-4	0.35 %
Water absorption rate		ISO 62	0.010 %

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.