PC/ABS CYCOLOY™ C1200HF-100 SABIC INNOVATIVE CHONGQING
208
- Unit Price:US$ 2,484 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:105MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:High impact resistance｜heat-resisting
- Application Areas:Electrical field｜Electronic field｜Automotive interior parts
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ASTM D1238 | 19 g/10 min | |
| Shrinkage rate | 内部方法 | 0.50 - 0.70 % |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 2270 Mpa | |
| tensile strength | ASTM D638 | 57.0 Mpa | |
| elongation | ASTM D638 | 5.0 % | |
| ASTM D638 | 100 % | ||
| Flexural modulus | ASTM D790 | 2340 Mpa | |
| bending strength | ASTM D790 | 88.0 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Dart impact | ASTM D3763 | 54.0 J | |
| ASTM D3763 | 54.0 J |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 2 | |
| High arc combustion index (HAI) | UL 746 | PLC 1 | |
| Hot wire ignition (HWI) | UL 746 | PLC 3 |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 100 to 110 °C | ||
| drying time | 3.0 to 4.0 hr | ||
| Suggested maximum moisture content | 0.020 % | ||
| Suggested injection volume | 30 to 80 % | ||
| Hopper temperature | 60 to 80 °C | ||
| Temperature at the rear of the barrel | 250 to 290 °C | ||
| Temperature in the middle of the barrel | 255 to 295 °C | ||
| Temperature at the front of the material cylinder | 260 to 300 °C | ||
| Spray nozzle temperature | 275 to 300 °C | ||
| Processing (melt) temperature | 275 to 300 °C | ||
| Temperature | 60 to 90 °C | ||
| Back pressure | 0.300 to 0.700 Mpa | ||
| screw speed | 40 to 70 rpm | ||
| Exhaust hole depth | 0.038 to 0.076 mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ASTM D648 | 129 °C | |
| ASTM D648 | 112 °C | ||
| vicat | ISO 306/B50 | 130 °C | |
| Linear coefficient of thermal expansion | ASTM E831 | 7.2E-5 cm/cm/°C | |
| RTI Elec | UL 746 | 105 °C | |
| RTI Imp | UL 746 | 80.0 °C | |
| RTI | UL 746 | 105 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.