PC/ABS CYCOLAC™ XCY630 SABIC INNOVATIVE US
165
- Unit Price:US$ 2,290 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:20MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:High mobility｜High temperature resistance
- Application Areas:Home appliance components｜Electrical applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| MeltViscosity | ISO 11443 | 170 Pa·s | |
| melt mass-flow rate | ASTM D1238 | 26 g/10min | |
| Melt volume flow rate | ISO 1133 | 22.0 cm3/10min | |
| Shrinkage rate | 内部方法 | 0.50-0.70 % | |
| 内部方法 | 0.50-0.70 % | ||
| Water absorption rate | ISO 62 | 0.40 % | |
| ISO 62 | 0.15 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| bending strength | ISO 178 | 82.0 Mpa | |
| ASTM D790 | 89.0 Mpa | ||
| tensile strength | ASTM D638 | 54.0 Mpa | |
| ISO 527-2/50 | 54.0 Mpa | ||
| ASTM D638 | 53.0 Mpa | ||
| ISO 527-2/50 | 53.0 Mpa | ||
| elongation | ASTM D638 | 4.5 % | |
| Tensile strain | ISO 527-2/50 | 4.5 % | |
| elongation | ASTM D638 | 120 % | |
| Tensile strain | ISO 527-2/50 | 120 % | |
| Flexural modulus | ASTM D790 | 2300 Mpa | |
| ISO 178 | 2200 Mpa | ||
| Tensile modulus | ASTM D638 | 2300 Mpa | |
| ISO 527-2/1 | 2250 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | 30 kJ/m² | |
| ISO 179/1eA | 65 kJ/m² | ||
| Impact strength of cantilever beam gap | ISO 180/1A | 30 kJ/m² | |
| ISO 180/1A | 65 kJ/m² | ||
| Dart impact | ASTM D3763 | 67.0 J | |
| ASTM D3763 | 55.0 J |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms | |
| Volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| dielectric strength | IEC 60243-1 | 35 KV/mm | |
| IEC 60243-1 | 25 KV/mm | ||
| IEC 60243-1 | 17 KV/mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ISO 75-2/Bf | 126 °C | |
| ASTM D648 | 107 °C | ||
| ISO 75-2/Af | 105 °C | ||
| vicat | ASTM D152510 | 126 °C | |
| ISO 306/B50 | 126 °C | ||
| ISO 306/B120 | 127 °C | ||
| ball-indentation hardness | IEC 60695-10-2 | Pass | |
| Linear coefficient of thermal expansion | ASTME831 | 7E-05 cm/cm/°C | |
| ISO 11359-2 | 8E-05 cm/cm/°C | ||
| ASTME831 | 7E-05 cm/cm/°C | ||
| ISO 11359-2 | 8E-05 cm/cm/°C | ||
| thermal conductivity | ISO 8302 | 0.20 W/m/K |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.