optical performance	Test Condition	Test Method	Test Result	Test Unit
gloss	45°,25.0μm	ASTM D2457	61
turbidity	25.0μm	ASTM D1003	8.0	%
other	Test Condition	Test Method	Test Result	Test Unit
purpose			薄膜.内衬袋.农业膜.拉链袋.气泡膜.发泡膜.发泡片材（珍珠棉）.交联发泡
characteristic			添加剂：抗氧化剂.滑爽剂.开口剂
remarks			薄膜级
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Friction coefficient		ASTM D1894	0.10
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	190°C/2.16kg	ISO 1133	2.5	g/10min
film	Test Condition	Test Method	Test Result	Test Unit
Elmendorf tear strength	TD:25μm	ISO 6383-2	25000	N
Tensile modulus	TD:25μm	ISO 527-3	216	Mpa
Tensile modulus	Tensile modulus	MD:25μm	ISO 527-3	194	Mpa
film thickness			20to100µm
film thickness	film thickness			25	µm
Elmendorf tear strength	MD:25μm	ISO 6383-2	70000	N
Dart impact	25μm	ASTM D1709	77	g
elongation	TD:Break,25μm	ISO 527-3	580	%
elongation	elongation	MD:Break,25μm	ISO 527-3	130	%
tensile strength	TD:Break,25μm	ISO 527-3	25.0	Mpa
tensile strength	tensile strength	MD:Break,25μm	ISO 527-3	70.0	Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.