thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion		ASTM E831	3.8E-5 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion		ISO 11359-2	5.5E-5 cm/cm/°C

Mechanical properties	Test Condition	Test Method	Test Result
tensile strength		ASTM D638	139 Mpa
tensile strength	tensile strength		ISO 527-2	138 Mpa
elongation		ASTM D638	2.1 %
flexural modulus		ISO 178	9700 Mpa
bending strength		ASTM D790	236 Mpa
bending strength	bending strength		ISO 178	211 Mpa
coefficient of friction		ASTM D3702	0.58
Wear factor		ASTM D3702	2.4E+6 10^-8 mm³/N·m

Impact resistance	Test Condition	Test Method	Test Result
Dart impact		ASTM D3763	10.0 J
Dart impact	Dart impact		ISO 6603-2	2.00 J

injection	Test Condition	Test Method	Test Result
drying temperature			80 °C
drying time			4.0 hr
Suggested maximum moisture content			0.15 to 0.25 %
Temperature at the rear of the barrel			265 to 275 °C
Temperature in the middle of the barrel			280 to 295 °C
Temperature at the front of the material cylinder			295 to 305 °C
Processing (melt) temperature			280 to 305 °C
mold temperature			95 to 110 °C
Back pressure			0.200 to 0.300 Mpa
screw speed			30 to 60 rpm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.