PA66

PA66 LNP™ LUBRICOMP™ RX01075 BK1B598BZDD SABIC INNOVATIVE US

272

Unit Price:US$ 19,366 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

For more details, please contact the supplier!

Material Description

Material Properties:Easy to form｜Filler: Glass fiber reinforced material｜40% filler by weight
Application Areas:Electronic and Electrical Applications｜Lighting applications
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	23°C	ISO 180/1A	16 kJ/m²
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	86 kJ/m²
Dart impact	23°C,TotalEnergy	ASTM D3763	18.0 J
Multi axis Instrumented Impact Energy		ISO 6603-2	4.00 J

mechanical properties	Test Condition	Test Method	Test Result
Tensile strain	Yield	ISO 527-2/5	2.9 %
elongation	Break	ASTM D638	2.9 %
Tensile strain	Break	ISO 527-2/5	2.9 %
Bending modulus	50.0mmSpan	ASTM D790	12400 Mpa
Bending modulus	Bending modulus		ISO 178	11200 Mpa
bending strength		ISO 178	229 Mpa
	bending strength	Yield,50.0mmSpan	ASTM D790	338 Mpa
	bending strength	bending strength	Break,50.0mmSpan	ASTM D790	337 Mpa
Tensile modulus		ASTM D638	13900 Mpa
Tensile modulus	Tensile modulus		ISO 527-2/1	14100 Mpa
tensile strength	Yield	ASTM D638	230 Mpa
	tensile strength	Yield	ISO 527-2/5	232 Mpa
		tensile strength	Break	ASTM D638	210 Mpa
		tensile strength	tensile strength	Break	ISO 527-2/5	232 Mpa
elongation	Yield	ASTM D638	2.8 %

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	260 °C
	Hot deformation temperature	0.45MPa,Unannealed,64.0mmSpan	ISO 75-2/Bf	259 °C
		Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	253 °C
		Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	244 °C
Linear coefficient of thermal expansion	MD：-30to30°C	ASTM D696	3.2E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：-30to30°C	ASTM D696	6.2E-05 cm/cm/°C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	MD：24hr	ASTM D955	0.20-0.40 %
Shrinkage rate	Shrinkage rate	TD：24hr	ASTM D955	1.0-3.0 %
Water absorption rate	24hr,50%RH	ASTM D570	0.66 %
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	1.0 %

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PA66 LNP™ LUBRICOMP™ RX01075 BK1B598BZDD SABIC INNOVATIVE US

Material Description

Technical Data Sheet Compare

Technical Data Sheet