Material Properties:high strength｜Aging resistance｜Weather resistance｜Dimensional stability｜Chemical resistance
Application Areas:Industrial components｜Automotive Applications｜Electrical applications｜Applied in fields that require high performance levels｜As for the load-bearing parts in different industrial sectors
Color:--
Grade:Enhanced level

Technical Data Sheet

Other performance	Test Condition	Test Method	Test Result	Test Unit
Fiberglass content			20	%
machinability	Test Condition	Test Method	Test Result	Test Unit
Melt Temperature			250-270	°C
Mold temperature			60-100	°C
Basic Performance	Test Condition	Test Method	Test Result	Test Unit
density		ISO 1183	1.39	g/cm³
melt mass-flow rate		ISO 1133	20	cm3/10min
Water absorption rate			0.4	%
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		ISO 527-1/-2	6900	Mpa
tensile strength		ISO 527-1/-2	100	Mpa
elongation	Break		2.5	%
bending strength		ISO 178	151	Mpa
Impact strength of simply supported beam without notch	23 ℃		55	kJ/m²
Charpy Notched Impact Strength			7	kJ/m²
Ball Pressure Test		ISO 2039-1	153	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Combustibility		UL 94	HB
Hot deformation temperature	1.80 MPa		160	°C
Linear coefficient of thermal expansion		ISO 11359-1/-2	0.4	E-4/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	Across Flow		0.16	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.