PC Makrolon® 6487 COVESTRO GERMANY
336
- Unit Price:US$ 3,165 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Good demolding performance｜Medium viscosity｜Flame retardant｜High impact resistance｜UV curing｜Processability
- Application Areas:Electrical field｜Electronic field｜Automotive sector｜Household appliances｜Household appliances｜Architectural application field｜Barrel｜Medical Supplies｜disposable
- Color:--
- Grade:Injection grade
Material Certification
Technical Data Sheet
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Ball Pressure Test | ISO 2039-1 | 117 Mpa |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| RTI Elec | 1.5mm | UL 746 | 125 °C |
| RTI Str | 1.5mm | UL 746 | 125 °C |
| RTI Imp | 1.5mm | UL 746 | 115 °C |
| Linear coefficient of thermal expansion | TD：23to55°C | ISO 11359-2 | 6.5E-05 cm/cm/°C |
| thermal conductivity | 23°C | ISO 8302 | 0.20 W/m/K |
| Vicat softening temperature | -- | ISO 306/B120 | 141 °C |
| Ball Pressure Test | 135°C | IEC 60695-10-2 | Pass |
| Linear coefficient of thermal expansion | MD：23to55°C | ISO 11359-2 | 6.5E-05 cm/cm/°C |
| Vicat softening temperature | -- | ISO 306/B50 | 143 °C |
| Hot deformation temperature | 1.8MPa,Unannealed | ISO 75-2/A | 122 °C |
| Glass transition temperature | ISO 11357-2 | 141 °C | |
| Hot deformation temperature | 0.45MPa,Unannealed | ISO 75-2/B | 134 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| FlashIgnitionTemperature | ASTM D1929 | 470 °C | |
| SelfIgnition | ASTM D1929 | 550 °C | |
| UL flame retardant rating | 1.5mm | UL 94 | V-0 |
| 3.0mm | UL 94 | 5VA | |
| Burning wire flammability index | 1.5mm | IEC 60695-2-12 | 960 °C |
| 3.0mm | IEC 60695-2-12 | 960 °C | |
| Hot filament ignition temperature | 1.5mm | IEC 60695-2-13 | 900 °C |
| Extreme Oxygen Index | ISO 4589-2 | 36 % | |
| ApplicationofFlamefromSmallBurner MethodKandF | 2.00mm | DIN 53438-1,-3 | K1.F1 |
| Burning rate - US-FMVSS | >1.00mm | ISO 3795 | passed |
| Hot filament ignition temperature | 3.0mm | IEC 60695-2-13 | 930 °C |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Electrolytic corrosion | 23°C | IEC 60426 | A1 |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | TD | ISO 2577 | 0.60-0.80 % |
| MD | ISO 2577 | 0.60-0.80 % | |
| melt mass-flow rate | 300°C/1.2kg | ISO 1133 | 10 g/10min |
| Melt Volume Flow Rate (MVR) | 300°C/1.2kg | ISO 1133 | 9.00 cm3/10min |
| Apparent density | ISO 60 | 0.64 g/cm³ | |
| Shrinkage rate | TD:2.00mm3 | ISO 294-4 | 0.75 % |
| MD:2.00mm3 | ISO 294-4 | 0.70 % | |
| Water absorption rate | Saturation,23°C | ISO 62 | 0.30 % |
| Equilibrium,23°C,50%RH | ISO 62 | 0.12 % | |
| density | 23°C | ISO 1183 | 1.20 g/cm³ |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Compared to the anti leakage trace index | SolutionB | IEC 60112 | PLC 4 |
| Surface resistivity | IEC 60093 | 1E+16 ohms | |
| Volume resistivity | 23°C | IEC 60093 | 1E+16 ohms·cm |
| Dielectric strength | 23°C,1.00mm | IEC 60243-1 | 34 KV/mm |
| Relative permittivity | 23°C,100Hz | IEC 60250 | 3.10 |
| 23°C,1MHz | IEC 60250 | 3.00 | |
| Compared to the anti leakage trace index | SolutionA | IEC 60112 | PLC 3 |
| Dissipation factor | 23°C,100Hz | IEC 60250 | 8E-04 |
| 23°C,1MHz | IEC 60250 | 9E-03 |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Bending strain | 23°C | ISO 178 | 7.0 % |
| Tensile modulus | 23°C | ISO 527-2/1 | 2450 Mpa |
| bending strength | 3.5%Strain,23°C | ISO 178 | 75.0 Mpa |
| 23°C | ISO 178 | 99.0 Mpa | |
| tensile strength | Break,23°C | ISO 527-2/50 | 65.0 Mpa |
| Tensile strain | Yield,23°C | ISO 527-2/50 | 6.0 % |
| Break,23°C | ISO 527-2/50 | 120 % | |
| Nominal tensile fracture strain | 23°C | ISO 527-2/50 | >50 % |
| Bending modulus | 23°C | ISO 178 | 2450 Mpa |
| tensile strength | Yield,23°C | ISO 527-2/50 | 66.0 Mpa |
| impact performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | -30°C,Complete Break | ISO 7391 | 12 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | NoBreak |
| Charpy Notched Impact Strength | 23°C,Partial Break | ISO 7391 | 70 kJ/m² |
| Impact strength of cantilever beam gap | -30°C,Complete Break | ISO 7391 | 12 kJ/m² |
| 23°C,Partial Break | ISO 7391 | 65 kJ/m² | |
| Multi axis Instrumented Impact Energy | -30°C | ISO 6603-2 | 55.0 J |
| 23°C | ISO 6603-2 | 50.0 J | |
| Multi axis Instrumented Peak Impact Force | -30°C | ISO 6603-2 | 6000 N |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | NoBreak |
| Multi axis Instrumented Peak Impact Force | 23°C | ISO 6603-2 | 5200 N |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.