POM HOSTAFORM® C52021 BK CELANESE GERMANY
195
- Unit Price:US$ 2,852 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Chemical resistance｜antioxidant｜Hydrolysis resistance
- Application Areas:Bottle cap｜Electrical applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Linear coefficient of thermal expansion | 23-55℃ Longitudinal | ISO 11359 part 1/2 | 110 µm/m-℃ |
| melting temperature | DSC,10 K/min | ISO 3146 method C1b | 166 °C |
| Heat Deflection Temperature | 1.8MPa | ISO 75 part 1/2 | 106 °C |
| vicat | VST/B/50 | ISO 306 | 151 °C |
| Basic performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO 1183 | 1.41 g/cm | |
| Water absorption rate | 23℃and50%RH | ISO 62 | 0.2 % |
| 23℃ | ISO 62 | 0.65 % | |
| melt mass-flow rate | 39cm | ISO 1133 | 54.99 g/10min |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| dielectric constant | 1 MHz | IEC 60250 | 4.0 |
| 低频100 Hz | IEC 60250 | 4.0 | |
| dielectric strength | IEC 60243 part 1 | 35 KV/mm | |
| Dissipation Factor | 1 MHz | IEC 60250 | 0.005 |
| 低频100 Hz | IEC 60250 | 0.003 |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| flexural modulus | ISO 178 | 2800 Mpa | |
| Impact strength of simply supported beam without notch | 23℃ | ISO 179 1eU | 10 J/cm |
| Charpy Notched Impact Strength | 低温-30℃ | ISO 179 1eA | 0.5 J/cm |
| Impact strength of simply supported beam without notch | 低温-30℃ | ISO 179 1eU | 10 J/cm |
| Charpy Notched Impact Strength | 23℃ | ISO 179 1eA | 0.55 J/cm |
| Tensile creep modulus | 1 hour | ISO 899 part 1 | 2500 Mpa |
| 1000 hours | ISO 899 part 1 | 1300 Mpa | |
| ball-indentation hardness | 30秒数值 | ISO 2039 part 1 | 148 Mpa |
| tensile strength | 50mm/min，屈服 | ISO 527 part 1/2 | 65 Mpa |
| Elongation at break | 50mm/min | ISO 527 part 1/2 | 15 % |
| elongation | 50mm/min | ISO 527 part 1/2 | 7 % |
| Tensile modulus | 1mm/min | ISO 527 part 1/2 | 3000 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.