Material Properties:Electrical performance｜Flame retardant｜high strength｜Oil resistant｜High rigidity
Application Areas:Electrical applications｜Electrical components
Color:--
Grade:Injection grade

Technical Data Sheet Compare

thermal performance	Test Condition	Test Method	Test Result
maximum service temperature			220 °C
Linear coefficient of thermal expansion	（23-80）℃，干态		1.5-2/6-7
TEMPERATURE	在20000h/5000h，后拉伸强度下降50%时		138/157 °C
Heat Deflection Temperature	0.45MPa负荷，干态		250 °C
Heat Deflection Temperature	Heat Deflection Temperature	1.8MPa负荷，干态		250 °C
specific heat	干态		1.4 J/(g.K)
thermal conductivity	干态		0.34 W/(m.K)

Electrical performance	Test Condition	Test Method	Test Result
Compared to the Leakage Traceability Index (CTI)	干/湿		CTI 600 M
Compared to the Leakage Traceability Index (CTI)	Compared to the Leakage Traceability Index (CTI)	干/湿		CTI 600
loss angle	1MHz，干/湿		0.02/0.2
dielectric strength	K20/P50，干/湿		70/40 KV/mm
Surface Resistivity	干/湿		>10 Ω
volume resistivity	干/湿		10 Ω.cm
dielectric constant	1MHz，干/湿		3.6/5

mechanical properties	Test Condition	Test Result
Tensile yield stress (V=50mm/min)	干/湿	160/120 Mpa
Tensile creep modulus	1000h,湿	4250 Mpa
Charpy Notched Impact Strength	+23℃，干/湿	14/18 KJ/m
elongation	≤0.5%, +23℃，湿	4250 Mpa
Impact Strength	干/湿	2/10 J
Charpy Notched Impact Strength	+23℃，干/湿	70/70 KJ/m
Elongation at break	干/湿，V=50mm/min	3/4 %
Tensile modulus	干/湿	11000/8500 Mpa
ball-indentation hardness	干/湿	210 Mpa
Fracture stress (V=50mm/min)	干/湿	160/120 Mpa
flexural modulus	干/湿	9200 Mpa
Charpy Notched Impact Strength	30℃，干	65 KJ/m
Elongation at break	干/湿，V=50mm/min	3/4 %
Impact strength of cantilever beam gap	+23℃，干/湿	13/20 KJ/m

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.