PPO

PPO NORYL GTX™ GTX830-1710 SABIC INNOVATIVE JAPAN

346

Unit Price:US$ 4,740 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
65MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

For more details, please contact the supplier!

Material Description

Material Properties:dimensional stability ｜enhance｜High temperature resistance｜Hydrolysis resistance｜filler｜Glass fiber reinforced material｜30%｜Filler by weight
Application Areas:Electrical applications｜Industrial machinery
Color:--
Grade:Injection grade

Technical Data Sheet

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.5 mm	UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	Yield	ASTM D638	151 Mpa
tensile strength	tensile strength	Break	ASTM D638	158 Mpa
bending strength	Yield, 100 mm Span	ASTM D790	248 Mpa
Bending modulus	100 mm Span	ASTM D790	8580 Mpa
elongation	Break	ASTM D638	7.0 %

injection	Test Condition	Test Method	Test Result
Processing (melt) temperature			280 to 305 °C
Mold temperature			75 to 120 °C
Back pressure			0.300 to 1.40 Mpa
Screw speed			20 to 100 rpm
Exhaust hole depth			0.013 to 0.038 mm
Spray nozzle temperature			280 to 305 °C
Temperature at the front of the material cylinder			275 to 305 °C
Temperature in the middle of the barrel			270 to 305 °C
Temperature at the rear of the barrel			265 to 305 °C
Suggested injection volume			30 to 50 %
Suggested maximum moisture content			0.070 %
drying time			3.0 to 4.0 hr
drying temperature			95 to 105 °C

thermal performance	Test Condition	Test Method	Test Result
RTI Elec		UL 746	50.0 °C
Linear coefficient of thermal expansion	-20 to 150°C，Flow	ASTM E831	2.0E-5 - 3.1E-5 cm/cm/°C
Vicat softening temperature		ASTM D15255	248 °C
Hot deformation temperature	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	240 °C
Hot deformation temperature	Hot deformation temperature	0.45 MPa, Unannealed, 6.40 mm	ASTM D648	254 °C
RTI		UL 746	50.0 °C
RTI Imp		UL 746	50.0 °C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	Flow : 3.20 mm	Internal Method	0.20 - 0.30 %
Shrinkage rate	Shrinkage rate	Across FlowFlow : 3.20 mm	Internal Method	0.65 - 0.85 %
Water absorption rate	24 hr, 50% RH	ASTM D570	0.50 %
Water absorption rate	Water absorption rate	Equilibrium, 50% RH	ASTM D570	1.0 %

Electrical performance	Test Method	Test Result
Hot wire ignition	UL 746	PLC 0
High voltage arc tracing rate	UL 746	PLC 1
High arc combustion index	UL 746	PLC 2
Compared to the anti leakage trace index	UL 746	PLC 2
Arc resistance	ASTM D495	PLC 6

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Scale	ASTM D785	120

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PPO NORYL GTX™ GTX830-1710 SABIC INNOVATIVE JAPAN

Material Description

Technical Data Sheet Compare

Technical Data Sheet