Material Properties:Thermal stability｜Low temperature resistance｜Filler: carbon powder
Application Areas:Automotive components｜Electronic and electrical accessories
Color:--
Grade:Injection grade

Technical Data Sheet Compare

thermal performance	Test Method	Test Result
1.8MPa, Unanealed, 3.20mm	ASTM D648	111 °C
1.8MPa, Unanealed, 64.0mm span	ISO 75-2/Af	126 °C
vicat	ISO 306/A50	144 °C

Impact resistance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	23°C	ISO 179/1eA	26 kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	95 kJ/m²
0°C		ASTM D256	290 J/m
23°C		ASTM D256	360 J/m
0°C		ISO 180/1A	20 kJ/m²
23°C		ISO 180/1A	25 kJ/m²
	23°C		ASTM D4812	2100 J/m
	23°C	23°C		ISO 180/1U	130 kJ/m²
23°C,EnergyatPeakLoad		ASTM D3763	27.0 J
23°C,TotalEnergy		ASTM D3763	39.1 J

Electrical performance	Test Condition	Test Method	Test Result
Surface Resistivity		ASTM D257	4.8E+07 ohms
volume resistivity		ASTM D257	1.4E+07 ohms·cm

Physical properties	Test Condition	Test Method	Test Result
Melt volume flow rate	300°C/5.0kg	ISO 1133	16.0 cm3/10min
shrinkage rate	MD	内部方法	0.64 %
shrinkage rate	shrinkage rate	TD	内部方法	0.68 %

mechanical properties	Test Condition	Test Method	Test Result
yield		ISO 527-2/5	58.0 Mpa
fracture		ASTM D638	47.0 Mpa
	fracture		ISO 527-2/5	47.0 Mpa
		fracture		ASTM D638	19 %
		fracture	fracture		ISO 527-2/5	17 %
flexural modulus		ISO 178	2550 Mpa
bending strength	--8	ISO 178	92.0 Mpa
bending strength	bending strength	--9	ISO 178	90.0 Mpa
Fracture bending strain		ISO 178	7.8 %
--2		ASTM D638	2570 Mpa
yield		ASTM D638	58.0 Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.