ABS POLYLAC® PA-764B TAIWAN CHIMEI
304
- Unit Price:US$ 5,646 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:50MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:heat-resisting
- Application Areas:Home appliance components｜Fitness equipment｜Electronic field｜Electrical field
- Color:--
- Grade:Flame retardant grade
Material Certification
Technical Data Sheet
Compare
| other | Test Condition | Test Method | Test Result |
|---|---|---|---|
| notes | 在射出周期中勿将热融胶长期停留在加热管中 | ||
| 难燃性 耐光性 耐热性 | |||
| Color | - | ||
| purpose | 计算机配件 / 电子产品零配件 / 电动工具零配件 / 电视机外壳 / 事务机器等 |
| processability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Dry conditions | 80°C下烘料约2-3小时 | ||
| process temperature | 220-180 °C | ||
| 190-220 °C | |||
| 180-220°C °C | |||
| screw speed | - rpm | ||
| Temperature | 40-70°C °C | ||
| Melt Temperature | - °C | ||
| pressure | 20-50kg/cm² Mpa | ||
| 5-10kg/cm² Mpa | |||
| 50-80kg/cm² Mpa |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 12(2.2) kg·cm/cm(J/M)ft·lb/in | |
| elongation at break | ASTM D638/ISO 527 | - % | |
| Tensile modulus | ASTM D638/ISO 527 | - kg/cm²(MPa)[Lb/in²] | |
| tensile strength | ASTM D638/ISO 527 | 400（5.810） kg/cm²(MPa)[Lb/in²] | |
| elongation | ASTM D638/ISO 527 | 20 % | |
| Rockwell hardness | ASTM D785 | R-102 | |
| Flexural modulus | ASTM D790/ISO 178 | 23000（32000） kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 660（9.370） kg/cm²(MPa)[Lb/in²] | |
| Charpy Notched Impact Strength | ASTM D256/ISO 179 | - kg·cm/cm(J/M)ft·lb/in | |
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | - kg·cm/cm(J/M)ft·lb/in | |
| ASTM D256/ISO 179 | 16（3.0） kg·cm/cm(J/M)ft·lb/in | ||
| elongation at break | ASTM D638/ISO 527 | - % |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.16 | |
| Shrinkage rate | ASTM D955 | - % | |
| Water absorption rate | ASTM D570/ISO 62 | - % | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 2.8 g/10min | |
| ASTM D1238/ISO 1133 | 28 g/10min |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Combustibility (rate) | UL 94 | 2.5mm.V-0 3.2mm.5VA | |
| Hot deformation temperature (HDT) | ASTM D648/ISO 75 | 93（199） ℃（℉） | |
| ASTM D648/ISO 75 | 80（176） ℃（℉） | ||
| vicat | ASTM D1525/ISO R306 | 101（214） ℃（℉） | |
| Linear expansion coefficient | ASTM D696/ISO 11359 | - mm/mm.℃ |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.