PA66 Vydyne® 41H ASCEND USA
239
- Unit Price:US$ 3,982 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:33MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
+86 ********View
For more details, please contact the supplier!
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:Injection grade
Material Certification

Technical Data Sheet
impact performance | Test Condition | Test Method | Test Result |
---|---|---|---|
Impact strength of simply supported beam without notch | 23°C | ISO 179 | 无断裂 |
-30°C | ISO 179 | 无断裂 |
flammability | Test Condition | Test Method | Test Result |
---|---|---|---|
Burning rate | 2.00 mm | ISO 3795 | 12 mm/min |
3.00 mm | ISO 3795 | 7.9 mm/min | |
UL flame retardant rating | 0.75 mm | UL 94 | HB |
1.5 mm | UL 94 | HB | |
3.0 mm | UL 94 | HB | |
Burning wire flammability index | 0.75 mm | IEC 60695-2-12 | 725 °C |
1.5 mm | IEC 60695-2-12 | 725 °C | |
3.0 mm | IEC 60695-2-12 | 675 °C | |
Hot filament ignition temperature | 0.75 mm | IEC 60695-2-13 | 750 °C |
1.5 mm | IEC 60695-2-13 | 750 °C | |
3.0 mm | IEC 60695-2-13 | 700 °C |
mechanical properties | Test Condition | Test Method | Test Result |
---|---|---|---|
bending strength | 23°C | ISO 178 | 55.0 Mpa |
Bending modulus | 23°C | ISO 178 | 1800 Mpa |
Tensile strain | Break, 23°C | ISO 527-2 | 53 % |
tensile strength | Break, 23°C | ISO 527-2 | 49.0 Mpa |
Yield, 23°C | ISO 527-2 | 49.0 Mpa | |
Tensile modulus | 23°C | ISO 527-2 | 1790 Mpa |
injection | Test Condition | Test Method | Test Result |
---|---|---|---|
Processing (melt) temperature | 285 to 305 °C | ||
Mold temperature | 65 to 95 °C | ||
drying temperature | 80 °C | ||
drying time | 4.0 hr | ||
Suggested maximum material return ratio | 25 % | ||
Temperature at the rear of the barrel | 280 to 310 °C | ||
Temperature in the middle of the barrel | 280 to 310 °C | ||
Temperature at the front of the material cylinder | 280 to 310 °C | ||
Spray nozzle temperature | 280 to 310 °C |
thermal performance | Test Condition | Test Method | Test Result |
---|---|---|---|
RTI | 3.0 mm | UL 746 | 125 °C |
1.5 mm | UL 746 | 120 °C | |
0.75 mm | UL 746 | 115 °C | |
RTI Imp | 3.0 mm | UL 746 | 75.0 °C |
1.5 mm | UL 746 | 75.0 °C | |
0.75 mm | UL 746 | 75.0 °C | |
RTI Elec | 3.0 mm | UL 746 | 130 °C |
1.5 mm | UL 746 | 130 °C | |
0.75 mm | UL 746 | 130 °C | |
Linear coefficient of thermal expansion | Across Flow : 23 to 55°C, 2.00 mm | ISO 11359-2 | 1.2E-4 cm/cm/°C |
Flow : 23 to 55°C, 2.00 mm | ISO 11359-2 | 1.5E-4 cm/cm/°C | |
Melting temperature | ISO 11357-3 | 262 °C | |
Hot deformation temperature | 1.8 MPa, Unannealed | ISO 75-2/A | 56.0 °C |
Physical properties | Test Condition | Test Method | Test Result |
---|---|---|---|
Shrinkage rate | Flow : 2.00 mm | ISO 294-4 | 1.8 % |
横向Flow : 2.00 mm | ISO 294-4 | 1.6 % |
Electrical performance | Test Condition | Test Method | Test Result |
---|---|---|---|
Dielectric strength | 1.00 mm | IEC 60243 | 14 KV/mm |
Arc resistance | 3.00 mm | ASTM D495 | PLC 2 |
Compared to the anti leakage trace index | 3.00 mm | IEC 60112 | PLC 0 |
Volume resistivity | 0.750 mm | IEC 60093 | 1.0E+10 ohms·cm |
High arc combustion index | 0.75 mm | UL 746 | PLC 0 |
1.5 mm | UL 746 | PLC 0 | |
3.0 mm | UL 746 | PLC 0 | |
High voltage arc tracing rate | UL 746 | PLC 2 | |
Hot wire ignition | 0.75 mm | UL 746 | PLC 4 |
1.5 mm | UL 746 | PLC 4 | |
3.0 mm | UL 746 | PLC 3 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.