Plastic Raw Materials
PPO/PA

PPO/PA NORYL GTX™  GTX910 SABIC INNOVATIVE US

397
  • Unit Price:US$ 3,909 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    65MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:High mobility｜Chemical resistance｜High rigidity
  • Application Areas:Electrical applications｜electrical equipment
  • Color:--
  • Grade:Injection grade

Technical Data Sheet

impact performanceTest ConditionTest MethodTest Result
Dart impact-30°C, Energy at PeakASTM D376339.0 J
Dart impact23°C, Energy at PeakASTM D376350.0 J
flammabilityTest ConditionTest MethodTest Result
UL flame retardant rating1.5 mmUL 94HB
mechanical propertiesTest ConditionTest MethodTest Result
tensile strengthYieldASTM D63859.0 Mpa
tensile strengthBreakASTM D63855.0 Mpa
elongationBreakASTM D63860 %
Bending modulus100 mm SpanASTM D7902240 Mpa
bending strengthYield, 100 mm SpanASTM D79095.0 Mpa
injectionTest ConditionTest MethodTest Result
drying temperature95 to 105 °C
drying time3.0 to 4.0 hr
Suggested maximum moisture content0.070 %
Suggested injection volume30 to 50 %
Temperature at the rear of the barrel265 to 305 °C
Temperature in the middle of the barrel270 to 305 °C
Temperature at the front of the material cylinder275 to 305 °C
Spray nozzle temperature280 to 305 °C
Processing (melt) temperature280 to 305 °C
Mold temperature75 to 120 °C
Back pressure0.300 to 1.40 Mpa
Screw speed20 to 100 rpm
Exhaust hole depth0.013 to 0.038 mm
thermal performanceTest ConditionTest MethodTest Result
Hot deformation temperature0.45 MPa, Unannealed, 6.40 mmASTM D648193 °C
Hot deformation temperature1.8 MPa, Unannealed, 6.40 mmASTM D648143 °C
Vicat softening temperatureASTM D15254232 °C
Linear coefficient of thermal expansionFlow : -40 to 95°CASTM E8319.0E-5 cm/cm/°C
Linear coefficient of thermal expansionFlow : 60 to 138°CASTM E8311.3E-4 cm/cm/°C
Linear coefficient of thermal expansionAcross Flow : -40 to 95°CASTM E8319.0E-5 cm/cm/°C
Linear coefficient of thermal expansionAcross Flow : 60 to 138°CASTM E8311.3E-4 cm/cm/°C
RTI ElecUL 74650.0 °C
RTI ImpUL 74650.0 °C
RTIUL 74650.0 °C
Physical propertiesTest ConditionTest MethodTest Result
Shrinkage rateFlow : 130°C, 1hrASTM D9551.6 - 1.8 %
Shrinkage rateFlow : 3.20 mmInternal Method1.1 - 1.3 %
Shrinkage rateAcross FlowFlow : 3.20 mmInternal Method1.0 - 1.2 %
Water absorption rate24 hr, 50% RHASTM D5700.50 %
Water absorption rateEquilibrium, 50% RHASTM D5701.0 %
Electrical performanceTest ConditionTest MethodTest Result
Arc resistanceASTM D495PLC 7
Compared to the anti leakage trace indexUL 746PLC 1
High arc combustion indexUL 746PLC 0
High voltage arc tracing rateUL 746PLC 4
Hot wire ignitionUL 746PLC 3
hardnessTest ConditionTest MethodTest Result
Rockwell hardnessR-ScaleASTM D785116
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.