Material Description
- Material Properties:High mobility｜Good demolding performance｜Good forming performance
- Application Areas:Thin walled products｜lens｜Optical data storage｜Safety equipment｜container
- Color:--
- Grade:Injection grade
Material Certification
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ASTM D1238 | 25 g/10 min | |
| Shrinkage rate | 内部方法 | 0.50 - 0.70 % |
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| transmissivity | ASTM D1003 | 88.0 % | |
| Haze ratio | ASTM D1003 | 1.0 % |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-2 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | ASTM D638 | 62.0 Mpa | |
| ASTM D638 | 65.0 Mpa | ||
| elongation | ASTM D638 | 120 % | |
| Flexural modulus | ASTM D790 | 2300 Mpa | |
| bending strength | ASTM D790 | 93.0 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Dart impact | ASTM D3763 | 54.0 J | |
| Impact strength of cantilever beam gap | ASTM D1822 | 378 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 2 | |
| High arc combustion index (HAI) | UL 746 | PLC 1 | |
| High Voltage Arc Traceability Rate (HVTR) | UL 746 | PLC 2 | |
| Hot wire ignition (HWI) | UL 746 | PLC 2 |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 120 °C | ||
| drying time | 3.0 to 4.0 hr | ||
| Suggested maximum moisture content | 0.020 % | ||
| Suggested injection volume | 40 to 60 % | ||
| Temperature at the rear of the barrel | 250 to 270 °C | ||
| Temperature in the middle of the barrel | 260 to 280 °C | ||
| Temperature at the front of the material cylinder | 270 to 295 °C | ||
| Spray nozzle temperature | 265 to 290 °C | ||
| Processing (melt) temperature | 270 to 295 °C | ||
| Temperature | 70 to 95 °C | ||
| Back pressure | 0.300 to 0.700 Mpa | ||
| screw speed | 40 to 70 rpm | ||
| Exhaust hole depth | 0.025 to 0.076 mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ASTM D648 | 126 °C | |
| RTI Elec | UL 746 | 130 °C | |
| RTI Imp | UL 746 | 130 °C | |
| RTI | UL 746 | 130 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.